Feature: | Polycarbonate |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | ||||||||||||||
MVR (300°C/1.2 kg) 12 cm³/10 min; optical lens; medium viscosity; UV stabilized; easy release; injection molding - melt temperature 280 - 320°C; available in clear tints only; safety glasses | ||||||||||||||
General | ||||||||||||||
Form | Resin Pellets | |||||||||||||
Feature |
Outdoor | Easy Release | Clean/High Purity | |||||||||||
Good Thermal | Good Dimensional | High Impact | ||||||||||||
UL Yellow Card | E41613-233138 | |||||||||||||
Uses Lenses Optical Applications Safety Equipment | ||||||||||||||
Physical | Nominal Value | Test Method | ||||||||||||
Density / Specific Gravity(23 °C) | 1.20 g/cm³ | ISO 1183 | ||||||||||||
Apparent Bulk Density, Pellets | 0.66 g/cm³ | ISO 60 | ||||||||||||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 13 g/10min | ISO 1133 | ||||||||||||
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) | 12 cm³/10 min | ISO 1133 | ||||||||||||
Molding Shrinkage, Across Flow | ||||||||||||||
0.60 - 0.80 % | ISO 2577 | |||||||||||||
2 mm;500 bar;60x60x2mm;280 °C | 0.75 % | ISO 294-4 | ||||||||||||
Molding Shrinkage, Flow | ||||||||||||||
0.60 - 0.80 % | ISO 2577 | |||||||||||||
2 mm;500 bar;60x60x2mm | 0.70 % | ISO 294-4 | ||||||||||||
Water Absorption, Saturation(23 °C) | 0.30 % | ISO 62 | ||||||||||||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.12 % | ISO 62 | ||||||||||||
Ball Indentation Hardness | 116 MPa | ISO 2039-1 | ||||||||||||
Water Vapor Transmission Rate(85% RH;100 µm;23 °C) | 15 g/m²/24hr | ISO 15106-1 | ||||||||||||
Carbon Dioxide Permeability(25.4 µm;23 °C) | 16900 cm³/m²/bar/24hr | ISO 2556 | ||||||||||||
Mechanical | Nominal Value | Test Method | ||||||||||||
Tensile Modulus(23 °C) | 2400 MPa | ISO 527-2/1 | ||||||||||||
Tensile Stress, Yield(23 °C) | 67.0 MPa | ISO 527-2/50 | ||||||||||||
Tensile Stress, Break(23 °C) | 70.0 MPa | ISO 527-2/50 | ||||||||||||
Tensile Strain, Yield(23 °C) | 6.1 % | ISO 527-2/50 | ||||||||||||
Tensile Strain, Break(23 °C) | 130 % | ISO 527-2/50 | ||||||||||||
Nominal Tensile Strain at Break(23 °C) | > 50 % | ISO 527-2/50 | ||||||||||||
Tensile creep modulus 1 hr 1.0e+3 hr |
2200 MPa 1900 MPa |
ISO 899-1 | ||||||||||||
Flexural Modulus(2 mm/min;23 °C) 2400 MPa | ISO 178 | |||||||||||||
Flexural Stress 2 mm/min;23 °C 2 mm/min;3.5% Strain;23 °C |
98.0 MPa 74.0 MPa |
ISO 178 | ||||||||||||
Flexural Strain at Flexural Strength(2 mm/min;23 °C) 7.0 % | ISO 178 | |||||||||||||
Gas Permeation, Carbon Dioxide(100 µm) 3800 cm³/m²/bar/24hr | ISO 2556 | |||||||||||||
Gas Permeation, Nitrogen 25.4 µm 100 µm |
510 cm³/m²/bar/24hr 120 cm³/m²/bar/24hr |
ISO 2556 | ||||||||||||
Gas Permeation, Oxygen 25.4 µm 100 µm |
2760 cm³/m²/bar/24hr 670 cm³/m²/bar/24hr |
ISO 2556 | ||||||||||||
C harpy Notched Impact Strength, Complete Break(-30 °C;3 mm) | 14 kJ/m² | ISO 179 1eA | ||||||||||||
C harpy Notched Impact Strength, Partial Break(23 °C;3 mm) | 70 kJ/m² | ISO 179 1eA | ||||||||||||
C harpy Unnotched Impact Strength -60 °C -30 °C 23 °C |
No Break No Break No Break |
ISO 179 1eU | ||||||||||||
Notched Izod Impact Strength, Complete Break(-30 °C;3 15 kJ/m² mm) |
ISO 180/1A | |||||||||||||
Notched Izod Impact Strength, Partial Break(23 °C;3 mm)70 kJ/m² | ISO 180/1A | |||||||||||||
Multi-Axial Instrumented Impact Energy -30 °C 23 °C |
65.0 J 60.0 J |
ISO 6603-2 | ||||||||||||
Multi-Axial Instrumented Impact, Peak Force -30 °C 23 °C |
6300 N 5400 N |
ISO 6603-2 | ||||||||||||
Thermal | Nominal Value | Test Method | ||||||||||||
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
135 °C 123 °C |
ISO 75-2/B ISO 75-2/A |
||||||||||||
Glass Transition Temperature(10 °C;min) | 144 °C | ISO 11357-2 | ||||||||||||
Vicat Softening Temperature | 143 °C 144 °C |
ISO 306/B50 ISO 306/B120 |
||||||||||||
Ball Pressure Test(135 °C) | Pass | IEC 60695-10-2 | ||||||||||||
CLTE, Flow(23 - 55 °C) | 6.5E-5 cm/cm/°C | ISO 11359-2 | ||||||||||||
CLTE, Transverse(23 - 55 °C) | 6.5E-5 cm/cm/°C | ISO 11359-2 | ||||||||||||
Thermal Conductivity, Across Flow(23 °C) | 0.20 W/m-K | ISO 8302 | ||||||||||||
RTI Elec(1.5 mm) | 125 °C | UL 746 | ||||||||||||
RTI Imp(1.5 mm) | 115 °C | UL 746 | ||||||||||||
RTI Str(1.5 mm) | 125 °C | UL 746 | ||||||||||||
Flame Rating 2.5 mm 0.75 mm |
HB V-2 |
UL 94 | ||||||||||||
Oxygen Index, Procedure A | 28 % | ISO 4589-2 | ||||||||||||
Flash Ignition Temperature | 480 °C | ASTM D1929 | ||||||||||||
Self Ignition Temperature | 550 °C | ASTM D1929 | ||||||||||||
Electrical | Nominal Value | Test Method | ||||||||||||
Surface Resistivity | 1.0E+16 ohms | IEC 60093 | ||||||||||||
Volume Resistivity(23 °C) | 1.0E+16 ohms ·cm | IEC 60093 | ||||||||||||
Electric Strength(23 °C;1 mm) | 34 kV/mm | IEC 60243-1 | ||||||||||||
Relative Permittivity 100 Hz;23 °C 23 °C;1.0e+6 Hz |
3.10 3.00 |
IEC 60250 | ||||||||||||
Dissipation Factor 100 Hz;23 °C 23 °C;1.0e+6 Hz |
5.0E-4 9.0E-3 |
IEC 60250 | ||||||||||||
Comparative Tracking Index, Solution A | 250 V | IEC 60112 | ||||||||||||
Comparative Tracking Index, Solution B | 125 V | IEC 60112 | ||||||||||||
Optical | Nominal Value | Test Method | ||||||||||||
Refractive Index, Method A | 1.586 | ISO 489 | ||||||||||||
Transmittance | 89.0 % 89.0 % 88.0 % > 87.0 % |
ISO 13468-2 | ||||||||||||
1.0e+3 2.0e+3 3.0e+3 4.0e+3 |
µm µm µm µm |
|||||||||||||
Haze(3.0e+3 µm) | < 0.500 % | ISO 14782 | ||||||||||||
Abbe Number | 30.0 | |||||||||||||
Chemical | Nominal Value | Test Method | ||||||||||||
Electrolytical Corrosion(23 °C) | A1 | IEC 60426 | ||||||||||||
Processing | Nominal Value | |||||||||||||
Drying Temperature - Dry Air Dryer<Injection> | 120 °C | |||||||||||||
Drying Time - Dry Air Dryer<Injection> | 4.0 hr | |||||||||||||
Suggested Max Moisture<Injection> | < 0.020 % | |||||||||||||
Suggested Shot Size<Injection> | 30 - 70 % | |||||||||||||
Rear Temperature<Injection> | 250 - 270 °C | |||||||||||||
Middle Temperature<injection> | 270 - 290 °C | |||||||||||||
Front Temperature<Injection> | 285 - 305 °C | |||||||||||||
Nozzle Temperature<Injection> | 270 - 305 °C | |||||||||||||
Processing Temp, Melt<Injection> | 280 - 320 °C | |||||||||||||
Mold Temperature<Injection> | 70 - 110 °C | |||||||||||||
Back Pressure<Injection> | 10.0 - 20.0 MPa | |||||||||||||
Vent Depth <Injection> | 0.025 - 0.075 mm | |||||||||||||
Standard Melt Temperature<Injection> | 300 °C | |||||||||||||
Peripheral Screw Speed <Injection> | 0.05 - 0.2 m/s | |||||||||||||
Hold Pressure<Injection> | 50 - 75 % |