| Feature: | Plastics |
|---|---|
| CAS No.: | 25766-59-0 |
| Formula: | C6h4c(CH3)2c6h4oco2-]N |
| Samples: |
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier Power Panels ABS Power Outlets Car Batteries projectors; large all-in-ones coffee machines
https://forever-plastics.en.made-in-china.com/product-list-1.html
| Product Description | |||||
| Features: Lightfast; Heat Resistant; 2.5mm V-0; 2.5mm 5VB; 3.0mm 5VA Applications: Displays; Chassis; Modems; Power Panels; Power Outlets; Car Batteries; projectors; large all-in-ones; coffee machines; TV front and rear frames and car audio consoles Weather Resistant |
|||||
| General | |||||
| Form | Resin Pellets | ||||
| Feature | Outdoor | Good Thermal | |||
| UL Yellow Card E56070-565075 | |||||
| Light Covers Printer Parts Panel | |||||
| Uses Facsimile machine parts Projector Housing Socket | |||||
| Components Coffee Machine | |||||
| Physical Nominal Value Test Method | |||||
| Density / Specific Gravity(23 °C) 1. 16 g/cm³ ISO 1183 | |||||
| Melt Volume-Flow Rate, MVR(220 °C;10 kg) 26 cm³/ 10 min ISO 1133 | |||||
| Molding Shrinkage 0.30 - 0.60 % ISO 294 -4 | |||||
| Mechanical Nominal Value Test Method | |||||
| Tensile Strength, Yield(50 mm/min) 37.0 MPa ISO 527 -2/50 | |||||
| Tensile Strength, Break(50 mm/min) 29.0 MPa ISO 527 -2/50 | |||||
| Tensile Elongation, Break(50 mm/min) 10 % ISO 527 -2/50 | |||||
| Flexural Modulus(2 mm/min) 1800 MPa ISO 178 | |||||
| Flexural Strength(2 mm/min) 57.0 MPa ISO 178 | |||||
| C harpy Notched Impact Strength ISO 179 | |||||
| -30 °C 7.0 kJ/m² | |||||
| 23 °C 14 kJ/m² | |||||
| Notched Izod Impact ISO 180/1A | |||||
| -30 °C 7.0 kJ/m² | |||||
| 23 °C 14 kJ/m² | |||||
| Thermal Nominal Value | Test Method | ||||
| Deflection Temperature Under Load, Unannealed(1.8 MPa) | 83.0 °C | ISO 75-2/A | |||
| Deflection Temperature Under Load, Annealed(1.8 MPa) | 93.0 °C | ISO 75-2/A | |||
| Vicat Softening Temperature | |||||
| 5 kg;50 ºC/hr | 90.0 °C | ISO 306/B50 | |||
| 50 ºC/hr;1 kg | 102 °C | ISO 306/A50 | |||
| CLTE, Flow | 8.6E-5 cm/cm/°C | ISO 11359-2 | |||
| Flame Rating 2.5 mm 2.5 mm 3 mm |
V-0 5VB 5VA |
UL 94 | |||
| Processing | Nominal Value | ||||
| Drying Temperature<Injection> | 80 - 85 °C | ||||
| Drying Time<Injection> | 2.0 - 4.0 hr | ||||
| Rear Temperature<Injection> | 180 - 210 °C | ||||
| Middle Temperature<injection> | 190 - 220 °C | ||||
| Front Temperature<Injection> | 190 - 220 °C | ||||
| Mold Temperature<Injection> | 40 - 70 °C | ||||
| Injection Pressure<Injection> | 4.90 - 7.85 MPa | ||||
| Injection Rate<Injection> | Slow-Moderate | ||||
| Holding Pressure<Injection> | 1.96 - 4.90 MPa | ||||
| Back Pressure<Injection> | 0.490 - 0.981 MPa | ||||
| Cushion<Injection> | 3.18 mm | ||||