Resin Pellets PPA with 45 % Glass Fiber for High Mechanical Strength And Rigidity
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
General | ||||||
Form Resin Pellets | ||||||
Filler 45 % Glass Fiber | ||||||
Feature |
High Mechanical Strength | Good Thermal High Strength |
Good Dimensional | |||
And Rigidity | ||||||
Uses | Automotive Under The Hood | Gaskets Racks | ||||
Physical Nominal Value Test Method | ||||||
Density / Specific Gravity 1.58 g/cm³ ISO 1183 | ||||||
Molding Shrinkage, Flow 0.1 - 0.3 % ISO 294-4 | ||||||
Molding Shrinkage, Across Flow 0.4 - 0.6 % ISO 294-4 | ||||||
Moisture Absorption 0.3 % ISO 62 | ||||||
Mechanical Nominal Value Test Method | ||||||
Tensile Strength(20 mm/min) 215 MPa ISO 527-2 | ||||||
Elongation at Break(20 mm/min) 2.6 % ISO 527-2 | ||||||
Flexural Strength(2 mm/min) 320 MPa ISO 178 | ||||||
Flexural Modulus(2 mm/min) 15000 MPa ISO 178 | ||||||
Notched Izod Impact Strength 14 kJ/m² ISO 180 | ||||||
Thermal Nominal Value Test Method | ||||||
Deflection Temperature(1.8 MPa) 290 °C ISO 75 | ||||||
Flammability(1.6 mm) HB UL94 | ||||||
Processing Nominal Value | ||||||
Drying Temperature 130 - 150 °C | ||||||
Drying Time 2 - 4 | ||||||
Mold Temperature 120 - 150 °C | ||||||
Melt Temperature 290 - 330 °C |