Product Description |
General purpose grade. Good clarity, heat resistance, property retention and dimensional stability. |
General |
Form |
Resin Pellets |
|
Feature |
Good Dimensional |
Good Thermal |
UL Yellow Card E207780-228431 |
Appliances |
Lighting Applications |
Automotive Lighting |
|
|
Nuclear Power |
Uses |
|
|
Pharmaceuticals |
3d Printing |
Automotive Exterior |
Automotive Interior |
Household Applications |
|
Physical |
Nominal Value |
Test Method |
Density / Specific Gravity |
1.20 g/cm³ |
ASTM D792 |
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) |
25 g/10min |
ASTM D1238 |
Molding Shrinkage, Flow(3.2 mm) |
0.50 - 0.70 % |
Internal Method |
Water Absorption(24 hr) |
0.10 % |
ASTM D570 |
Water Absorption, Equilibrium |
|
ASTM D570 |
23 °C |
0.35 % |
|
100 °C |
0.58 % |
|
Mechanical |
Nominal Value |
Test Method |
Tensile Strength, Yield(50 mm/min;Type I) |
62.0 MPa |
ASTM D638 |
Tensile Strength, Break(50 mm/min;Type I) |
65.0 MPa |
ASTM D638 |
Tensile Elongation, Break(50 mm/min;Type I) |
120 % |
ASTM D638 |
Flexural Modulus(1.3 mm/min;50 mm;Span) |
2300 MPa |
ASTM D790 |
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) |
93.0 MPa |
ASTM D790 |
Notched Izod Impact(23 °C) |
640 J/m |
ASTM D256 |
Instrumented Dart Impact, Energy at Peak(23 °C) |
54.0 J |
ASTM D3763 |
Tensile Impact Strength(Type S) |
378 kJ/m² |
ASTM D1822 |
Thermal |
Nominal Value |
Test Method |
Deflection Temperature Under Load, Unannealed(1.8 MPa;3.2 mm) |
126 °C |
ASTM D648 |
RTI Elec |
130 °C |
UL 746 |
RTI Imp |
130 °C |
UL 746 |
RTI Str |
130 °C |
UL 746 |
Flame Rating(1.1 mm) |
V-2 |
UL 94 |
Electrical |
Nominal Value |
Test Method |
Comparative Tracking Index[CTI] |
PLC 2 |
UL 746 |
High Amp Arc Ignition, HAI, Surface |
PLC 1 |
UL 746 |
High Voltage Arc Tracking Rate, HVTR |
PLC 2 |
UL 746 |
Hot-wire Ignition, HWI |
PLC 2 |
UL 746 |
Optical |
Nominal Value |
Test Method |
Transmittance (2.5e+3 µm) |
88.0 % |
ASTM D1003 |
Haze(2.5e+3 µm) |
1.00 % |
ASTM D1003 |
Processing |
|
Nominal Value |
Drying Temperature<Injection> |
|
120 °C |
Drying Time<Injection> |
|
3.0 - 4.0 hr |
Suggested Max Moisture<Injection> |
|
0.020 % |
Suggested Shot Size<Injection> |
|
40 - 60 % |
Rear Temperature<Injection> |
|
250 - 270 °C |
Middle Temperature<injection> |
|
260 - 280 °C |
Front Temperature<Injection> |
|
270 - 295 °C |
Nozzle Temperature<Injection> |
|
265 - 290 °C |
Processing Temp, Melt<Injection> |
|
270 - 295 °C |
Mold Temperature<Injection> |
|
70 - 95 °C |
Back Pressure<Injection> |
|
0.300 - 0.700 MPa |
Screw Speed <Injection> |
|
40 - 70 rpm |
Vent Depth <Injection> |
|
0.025 - 0.076 mm |
Drying Time, Cumulative<Injection> |
|
48 hrs |