Product Description | |||||||
33 % glass reinforced, impact modified. Connectors, etc. | |||||||
General | |||||||
Form | Resin | Pellets | |||||
Filler | 33 % | Glass Fiber | |||||
UL Yellow Card E207780-100140794 | |||||||
Appliances Automotive Under The Electronic Displays | |||||||
Uses | oo | Automotive Exterior | |||||
Connector | Electrical | Medical | |||||
Physical | Nominal Value | Test Method | |||||
Density / Specific Gravity | 1.52 g/cm³ | ASTM D792 | |||||
Specific Volume | 0.650 cm³/g | ASTM D792 | |||||
Melt Mass-Flow Rate, MFR(250 °C;2.16 kg) | 12 g/10min | ASTM D1238 | |||||
Molding Shrinkage, Across Flow | Internal Method | ||||||
1.5 - 3.2 mm | 0.40 - 0.60 % | ||||||
3.2 - 4.6 mm | 0.60 - 0.90 % | ||||||
Molding Shrinkage, Flow | |||||||
1.5 - 3.2 mm | 0.30 - 0.50 % | Internal Method | |||||
3.2 mm | 0.50 % | Internal Method | |||||
3.2 - 4.6 mm | 0.50 - 0.80 % | ASTM D792;ISO | |||||
1183 | |||||||
Water Absorption(24 hr) | 0.050 % | ASTM D570 | |||||
Rockwell Hardness, R-Scale | 125 | ASTM D785 | |||||
Mechanical | Nominal Value | Test Method | |||||
Tensile Modulus(5 mm/min) | 8660 MPa | ASTM D638 | |||||
Tensile Strength, Break(5 mm/min;Type I) | 106 MPa | ASTM D638 | |||||
Tensile Elongation, Break(5 mm/min;Type I) | 3.1 % | ASTM D638 | |||||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 7810 MPa | ASTM D790 | |||||
Flexural Strength, Break(1.3 mm/min;50 mm;Span) | 174 MPa | ASTM D790 | |||||
Notched Izod Impact(23 °C) | 130 J/m | ASTM D256 | |||||
Unnotched Izod Impact(23 °C) | 860 J/m | ASTM D4812 | |||||
Thermal | Nominal Value | Test Method | |||||
Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;6.4 mm |
223 °C 208 °C |
ASTM D648 | |||||
RTI Elec | 130 °C | UL 746 | |||||
RTI Imp | 130 °C | UL 746 | |||||
RTI Str | 140 °C | UL 746 | |||||
Flame Rating(1.5 mm) | HB | UL 94 | |||||
Electrical | Nominal Value | Test Method | |||||
Arc Resistance, Tungsten Electrode | PLC5 | ASTM D495 | |||||
Comparative Tracking Index, CTI | PLC 1 | UL 746 | |||||
High Amp Arc Ignition, HAI, Surface | PLC 2 | UL 746 | |||||
High Voltage Arc Tracking Rate, HVTR | PLC 0 | UL 746 | |||||
Hot-wire Ignition, HWI | PLC 0 | UL 746 | |||||
Processing | Nominal Value | ||||||
Drying Temperature<Injection> | 120 °C | ||||||
Drying Time<Injection> | 3.0 - 4.0 hr | ||||||
Suggested Max Moisture<Injection> | 0.020 % | ||||||
Suggested Shot Size<Injection> | 40 - 80 % | ||||||
Rear Temperature<Injection> | 240 - 255 °C | ||||||
Middle Temperature<injection> | 245 - 260 °C | ||||||
Front Temperature<Injection> | 250 - 265 °C | ||||||
Nozzle Temperature<Injection> | 245 - 260 °C | ||||||
Processing Temp, Melt<Injection> | 250 - 265 °C | ||||||
Mold Temperature<Injection> | 65 - 90 °C | ||||||
Back Pressure<Injection> | 0.300 - 0.700 MPa | ||||||
Screw Speed <Injection> | 50 - 80 rpm | ||||||
Vent Depth <Injection> | 0.025 - 0.038 mm | ||||||
Injection, Drying Time, Cumulative<Injection> | 12 hrs |