Product Description | |||||
PC 1302LT-12 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. Main Characteristics Medium viscosity UV absorbers No mold release agent Applications Luminaires Outdoor appliances Lens | |||||
General | |||||
Form | Resin Pellets | ||||
Feature | Clean/High Purity Medium Viscosity | Good Thermal Outdoor | Ductile | ||
Uses Appliances | Lenses | Outdoor | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792 | |||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 12 g/10min | ASTM D1238 | |||
Molding Shrinkage, Flow | 0.50 - 0.70 % | ASTM D955 | |||
Water Absorption(24 hr;23 °C) | 0.15 % | ASTM D570 | |||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.32 % | ASTM D570 | |||
Rockwell Hardness, M-Scale | 73 | ASTM D785 | |||
Rockwell Hardness, R-Scale | 118 | ASTM D785 | |||
Mechanical | Nominal Value | Test Method | |||
Tensile Modulus | 2380 MPa | ASTM D638 | |||
Tensile Strength, Yield(50 mm/min;23 °C) | 60.0 MPa | ASTM D638 | |||
Tensile Strength, Break | 71.0 MPa | ASTM D638 | |||
Tensile Elongation, Yield | 6.0 % | ASTM D638 | |||
Tensile Elongation, Break | 150 % | ASTM D638 | |||
Flexural Modulus | 2410 MPa | ASTM D790 | |||
Flexural Strength | 96.0 MPa | ASTM D790 | |||
Taber Abrasion Resistance - Delta Haze(CS-10F Wheel;1.0e+3 g;500 Cycles) | 45 % | ASTM D1044 | |||
Notched Izod Impact(23 °C;3.18 mm;0.25 mm;Notch Depth) | 880 J/m | ASTM D256 | |||
Unnotched Izod Impact(23 °C) | No Break | ASTM D256 | |||
Instrumented Dart Impact, Total Energy(23 °C;3.39 m/sec;3.18 mm) | 87.0 J | ASTM D3763 | |||
Thermal | Nominal Value | Test Method | |||
Deflection Temperature Under Load, Annealed 0.45 MPa;4 mm 1.8 MPa;4 mm |
143 °C 141 °C |
ASTM D648 | |||
Deflection Temperature Under Load, Unannealed(1.8 MPa;4 mm) | 127 °C | ASTM D648 | |||
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 148 °C | ASTM D1525 | |||
CLTE, Flow(-40 - 82 °C) | 6.8E-5 cm/cm/°C | ASTM D696 | |||
Optical | Nominal Value | Test Method | |||
Refractive Index | 1.586 | ASTM D542 | |||
Transmittance | > 90.0 % | ASTM D1003 | |||
Haze | 0.700 - 1.50 % | ASTM D1003 |