Polyamine Nylon66 High Strength and Stiffness Combined with High Heat Deflection

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA66-GF40
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Polyamine Nylon66 high strength and stiffness combined with high heat deflection
 Heat-conducting nylon

Product Description

Product Description
Material code according PA66 Heat stabilized Nylon 66 reinforced by 40 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.
General
Form		Resin Pellets
Filler		40 % Long Glass Fiber
Feature		Low Warpage	Corrosion Resistant	Creep Resistance
		Good Dimensional
Uses		Metal Replacement
Physical			Nominal Value	Test Method
Density, dry			1.46 g/cm³	ISO 1183
Condition: Density			1.46 g/cm³	ISO 1183
Mechanical			Nominal Value	Test Method
Dry: Tensile Modulus			13700 MPa	ISO 527-2/1A
Condition: Tensile Modulus			10000 MPa	ISO 527-2/1A
Dry: Tensile Stress, Break			190 MPa	ISO 527-2/1A/5
Condition: Tensile Stress, Break			160 MPa	ISO 527-2/1A/5
Dry: Tensile Strain, Break			1.6 %	ISO 527-2/1A/5
Condition: Tensile Strain, Break			2.0 %	ISO 527-2/1A/5
Dry: Flexural Modulus 23 °C 80 °C			12600 MPa 8000 MPa	ISO 178
Condition: Flexural Modulus 23 °C 80 °C			10000 MPa 7000 MPa	ISO 178
Dry: Flexural Stress 23 °C 80 °C			260 MPa 250 MPa	ISO 178
Condition: Flexural Stress 23 °C 80 °C			250 MPa 210 MPa	ISO 178
Dry: Charpy Notched Impact Strength -30 °C 23 °C			23 kJ/m² 23 kJ/m²	ISO 179 1eA
Condition: Charpy Notched Impact Strength(23 °C)			18 kJ/m²	ISO 179 1eA
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C			41 kJ/m² 40 kJ/m²	ISO 179 1eU
Condition: Charpy Unnotched Impact Strength(23 °C)			45 kJ/m²	ISO 179 1eU
Dry: Notched Izod Impact Strength -30 °C 23 °C			35 kJ/m² 24 kJ/m²	ISO 180/1A
Notched Izod Impact Strength: condition(23 °C)			19 kJ/m²	ISO 180/1A
Thermal			Nominal Value	Test Method
Dry: Heat Deflection Temperature, Unannealed
1.8 MPa			255 °C	ISO 75-2/A
8 MPa			240 °C	ISO 75-2/C
Dry: Melting Temperature(10 °C;min)			261 °C	ISO 11357-3
Processing				Nominal Value
Drying Temperature<Injection>				70 - 80 °C
Drying Time<Injection>				2.0 - 4.0 hr
Suggested Max Moisture<Injection>				0.15 %
Hopper Temperature<Injection>				70 - 80 °C
Rear Temperature<Injection>				265 - 275 °C
Middle Temperature<injection>				275 - 285 °C
Front Temperature<Injection>				285 - 295 °C
Nozzle Temperature<Injection>				305 - 315 °C
Processing Temp, Melt<Injection>				305 - 315 °C
Mold Temperature<Injection>				90 - 120 °C
Injection Rate<Injection>				Moderate
Back Pressure<Injection>				< 3.00 MPa
Feeding Zone Temperature<Injection>				20 - 50 °C
Zone4 temperature<Injection>				295 - 305 °C
Hot Runner Temperature<Injection>				300 - 315 °C

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 