Product Description | |||||
General Purpose Grade CHARACTERISTICS: High impact, High gloss. | |||||
General | |||||
Form | |||||
Feature | |||||
UL Yellow Card E162823-224714 | |||||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity 23 °C 23 °C |
1.04 g/cm³ 1.04 g/cm³ |
ASTM D792 ISO 1183 |
|||
Melt Mass-Flow Rate, MFR 200 °C;5 kg 220 °C;10 kg |
2.1 g/10min 21 g/10min |
ASTM D1238;ISO 1133 |
|||
Rockwell Hardness, R-Scale(23 °C) | 107 | ASTM D785;ISO 2039-2 |
|||
Mechanical | Nominal Value | Test Method | |||
Tensile Strength(23 °C) | 43.0 MPa | ASTM D638;ISO 527-2 |
|||
Flexural Modulus(23 °C) | 2250 MPa | ASTM D790;ISO 178 |
|||
Flexural Strength(23 °C) | 63.0 MPa | ASTM D790;ISO 178 |
|||
Notched Izod Impact(23 °C;6.35 mm) | 25 J/m | ASTM D256 | |||
Thermal | Nominal Value | Test Method | |||
Deflection Temperature Under Load, Unannealed(1.8 MPa;12.7 mm) | 86.0 °C | ISO 75-2/A;ASTM D648 |
|||
Deflection Temperature Under Load, Annealed(1.8 MPa;120?/h) | 95.0 °C | ISO 75-2/A;ASTM D648 |
|||
Vicat Softening Temperature(50 N;Loading 2) | 89.0 °C | ASTM D1525;ISO 306/B | |||
Flame Rating, All Colors(1.5 mm) | HB | UL 94 |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |