Polyamide 6 20% Glass Fiber and Mineral Filler Heat-Aging Stabilized

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA6-C 60 MX10 V10
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Polyamide 6 20% glass fiber and mineral filler heat-aging stabilized
 Heat-conducting nylon

Product Description

Product Description
Polyamide 6, 20% glass fiber and mineral filler, heat-aging stabilized, halogen and red phosphorus free flame retardant, for injection moulding
General
Form	Resin Pellets
Filler                                         10 % Glass Fiber               10 % Mineral
				Non-Brominated &  Non-
Feature				Chlorinated Flame
				Retardant
Physical		Nominal Value		Test Method
Density / Specific Gravity		1.37 g/cm³		ISO 1183
Mechanical		Nominal Value		Test Method
Tensile Modulus(1 mm/min)		7900 MPa		ISO 527-1/-2
Stress at break(5 mm/min)		85 MPa		ISO 527-1/-2
Strain at break(5 mm/min)		3 %		ISO 527-1/-2
Flexural Modulus(2 mm/min)		6500 MPa		ISO 178
Flexural Strength(2 mm/min)		120 MPa		ISO 178
C harpy Impact Strength, Unnotched(23 °C)		35 kJ/m²		ISO 179/1eU
C harpy Notched Impact Strength(23 °C)		4.5 kJ/m²		ISO 179/1eA
Izod impact strength, Notched(23 °C)		30 kJ/m²		ISO 180/1U
Notched Izod Impact Strength(23 °C)		4.5 kJ/m²		ISO 180/1A
Thermal		Nominal Value		Test Method
Melting Temperature(10 °C/min)		221 °C		ISO 11357-1
Flammability				UL 94
0.75 mm		V-0
1.5 mm		V-0
3 mm		V-0
Glow Wire Flammability Index(1 - 3 mm)		960 °C		IEC 60695-2-12
Glow Wire Ignition Temperature [GWIT](1 - 3 mm)		750 °C		IEC 60695-2-13
Burning rate(1 mm)		< 100 mm/min		FMVSS 302
Electrical		Nominal Value		Test Method
Volume Resistivity		1E+11 ohms ·cm		IEC 62631-3-1
Surface Resistivity		1.0E+13 Ohms		IEC 62631-3-1
Comparative Tracking Index(Solution A)		575 V		IEC 60112
Processing			Nominal Value
Drying Temperature			75 - 85 °C
Dry Time(with dew point of dried air < -30 °C)			2 - 4 h
Melt Temperature			240 - 260 °C
Mold Temperature			70 - 90 °C

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 