Features: Good flame retardancy; Heat resistance; 0.75mm V-2; 1.0mm V-0; 2.5mm 5VA Application: Display; Chassis; Modem; Power Panel; Power Outlet; Car Battery; Cash Register Housing; Printer Housing; Remote controls; light boxes; fax machines; projectors; large MFPs; coffee machines; TV front and rear frames and car audio consoles | ||||
General | ||||
Form | ||||
Feature | Good Thermal Flame Retardant Outdoor | |||
UL Yellow Card E56070-103035269 | ||||
Uses |
Batteries Light Covers Facsimile machine parts Automotive Coffee Machine |
Displays Printer Parts Projector Housing Printer Chassis |
Housing Panel Socket Remote Controls |
|
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity(23 °C) | 1.22 g/cm³ | ISO 1183 | ||
Melt Volume-Flow Rate, MVR(220 °C;10 kg) | 34 cm³/10 min | ISO 1133 | ||
Molding Shrinkage | 0.30 - 0.60 % | ISO 294-4 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Stress, Yield(50 mm/min) | 34.0 MPa | ISO 527-2/50 | ||
Tensile Stress, Break(50 mm/min) | 27.0 MPa | ISO 527-2/50 | ||
Tensile Strain, Break(50 mm/min) | 10 % | ISO 527-2/50 | ||
Flexural Modulus(2 mm/min) | 1800 MPa | ISO 178 | ||
Flexural Stress(2 mm/min) | 54.0 MPa | ISO 178 | ||
Charpy Notched Impact Strength -30 °C 23 °C |
7.0 kJ/m² 12 kJ/m² |
ISO 179 | ||
Notched Izod Impact Strength -30 °C 23 °C |
7.0 kJ/m² 13 kJ/m² |
ISO 180/1A |
Thermal | Nominal Value | Test Method | |
Deflection Temperature Under Load, Unannealed(1.8 MPa) | 82.0 °C | ISO 75-2/A | |
Deflection Temperature Under Load, Annealed(1.8 | MPa) 92.0 °C | ISO 75-2/A | |
Vicat Softening Temperature | |||
5 kg;50 ºC/hr | 90.0 °C | ISO 306/B50 | |
50 ºC/hr;1 kg | 101 °C | ISO 306/A50 | |
CLTE, Flow | 8.3E-5 cm/cm/°C | ISO 11359-2 | |
Flame Rating 0.75 mm 1 mm 2.5 mm |
V-2 V-0 5VA |
UL 94 | |
Processing | Nominal Value | ||
Drying Time | 80 - 85 °C | ||
Drying Temperature | 2 - 4 h | ||
Barrell Temperature - Front | 190 - 220 °C | ||
Barrell Temperature - Middle | 190 - 220 °C | ||
Barrell Temperature - Rear | 180 - 210 °C | ||
Mold Temperature | 40 - 70 °C | ||
Injection Pressure | 50 - 80 % | ||
Hold Pressure | 20 - 50 % | ||
Back Pressure | 0.5 - 1 MPa |