POM Raw Material or Modified Reinforced for Industrial Products and Toys, Textile Industry

• Flame Retardant: 0.75mm 1.5mm V0 5va
• Heat Resistance: High
• Transmitance: >90%
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: SlideXTM2404
• Mfi: 3 5 8 10 12 ....
• Process: Injection Extrusion
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 50.00cm * 15.00cm
• Package Gross Weight: 25.000kg

Product Description

POM raw material or modified reinforced for industrial products and toys, textile industry

 

Product Description
Hostaform® MT® SlideXTM2404 is a low melt viscosity injection molding grade for fast cycling and thin walled    parts with tribological modification designed for use in demanding applications that require prevention of audible noise caused by stick-slip phenomenon and low friction and wear against plastics and metals. Hostaform® MT      SlideXTM 2404 is a special grade developed for medical industry applications and complies with: CFR 21                (177.2470) of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 11559) and the   Device Master File (MAF 1079) the corresponding EU and national registry regulatory requirements                         biocompatibility in tests corresponding to USP <88> Class VI/ISO 10993 low residual monomers no animal-  derived constituents
General
Form	Resin Pellets
Biocompatible                  Medium-Low Viscosity     Excellent Processability
Feature	No Animal Derived             Dmf 11559                          Fda
Components                      Maf
Uses	Thin-walled Parts              Medical
Physical		Nominal Value	Test Method
Density / Specific Gravity		1.40 g/cm³	ISO 1183
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg)		25 cm³/10 min	ISO 1133
Molding Shrinkage, Across Flow		1.8 %	ISO 294-4
Molding Shrinkage, Flow		1.9 %	ISO 294-4
Water Absorption, Saturation(23 °C)		0.60 %	ISO 62
Water Absorption, Equilibrium(50% RH;23 °C)		0.20 %	ISO 62
Ball Indentation Hardness(30s)		130 MPa	ISO 2039-1
Mechanical		Nominal Value	Test Method
Tensile Modulus		2550 MPa	ISO 527-2/1A
Tensile Stress, Yield		55.0 MPa	ISO 527-2/1A/50
Tensile Strain, Yield		7.0 %	ISO 527-2/1A/50
Nominal Tensile Strain at Break		50 %	ISO 527-2/1A/50
Flexural Modulus(23 °C)		2300 MPa	ISO 178
Charpy Notched Impact Strength			ISO 179 1eA
-30 °C		5.5 kJ/m²
23 °C		5.5 kJ/m²
Charpy Unnotched Impact Strength			ISO 179 1eU
-30 °C		150 kJ/m²
23 °C		160 kJ/m²

 

Thermal	Nominal Value	Test Method
Heat Deflection Temperature, Unannealed(1.8 MPa)	90.0 °C	ISO 75-2/A
Vicat Softening Temperature	144 °C	ISO 306/B50
Melting Point(10 °C/min)	166 °C	ISO 11357-3
CLTE, Flow	1.4E-4 cm/cm/°C	ISO 11359-2
CLTE, Transverse	1.4E-4 cm/cm/°C	ISO 11359-2
Processing		Nominal Value
Drying Temperature<Injection>		100 - 120 °C
Drying Time<Injection>		3.0 - 4.0 hr
Suggested Max Moisture<Injection>		0.15 %
Hopper Temperature<Injection>		20 - 30 °C
Rear Temperature<Injection>		170 - 175 °C
Middle Temperature<injection>		180 - 185 °C
Front Temperature<Injection>		180 - 195 °C
Nozzle Temperature<Injection>		190 - 200 °C
Processing Temp, Melt<Injection>		180 - 200 °C
Mold Temperature<Injection>		80 - 120 °C
Injection Rate<Injection>		Slow-Moderate
Back Pressure<Injection>		< 4.00 MPa
Feeding Zone Temperature<Injection>		60 - 80 °C
Zone4 temperature<Injection>		180 - 200 °C
Hot Runner Temperature<Injection>		190 - 200 °C

                                                                                                             Forever Co.,Ltd

Dongguan Forever Co.,Ltd With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021.
 

Our customers are Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....

High quality polycarbonate outdoor uses high UV resistant materials for LED lights monitoring lights security lights

 

 

 

ITEM NO: PC XH-25W-34
FEATURE:Light Shielding Polycarbonate,Injection Molding Grade,
Flammability Rating UL-94 V-0(1.0mm) /5VA(2.5mm),
        Weathering Rating UL746C F1 grade,with ordinary shading effect,
good low temperature resistance, good fluidity,
excellent molding performance, in line with environmental protection requirements
 

TYPICAL PROPERTIES		STANDARD	UNIT	TYPICAL VALUE
Physical Property	Specific Gravity	ISO1183	g/cm^3	1.23
	Melt Flow Rate(300ºC 1.2kg)	ISO1133	g/10min	11
	Water Absorption	ISO62	%	0.25
Mechanical Property	Tensile Strength(50mm/min)	ISO527	MPa	55
	Elongation at break(50mm/min)	ISO527	%	60
	Tensile Strength(50mm/min)	ISO527	MPa	2000
	Flexural Strength(2mm/min)	ISO178	MPa	90
	Flexural Modulus(2mm/min)	ISO178	2100	2100
	Notched Charpy Impact Strength(23ºC)	ISO180	KJ/m^2	50
	Notched Charpy Impact Strength(-35ºC/3H)	ISO180	KJ/m^2	30
Thermal Property	HDT (1.8MPa)	ISO75	ºC	120
	Linear expansion coefficient	ASTM D696	×10-5cm/cm/ºC	7.0
	Mold shrinkage	ASTM D955	%	0.5-0.7
	Flammability	UL94	--	V0(1.0mm) 5VA(2.5mm)
RTI	Elec	UL746B	ºC	130(1.0mm)
	Imp	UL746B	ºC	125(1.0mm)
	Str	UL746B	ºC	130(1.0mm)
UV	Weather Resistance	UL746C	F1 or F2	F1