| Feature: | Oxidative Degradable |
|---|---|
| Material: | Polyamide(Nylon 6.66)/PA |
| Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
| Samples: |
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier Polyamide (nylon 66) PA66 material , virgin PA plastic granule PA6 PA66 PA6.6 gf35 gf30https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html
2HEBV is a Polyamide 6 (Nylon 6) material filled with 20% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for blow molding or extrusion. Important attributes of EBV-2H are: Flame Rated RoHS Compliant Heat Stabilizer Typical applications include: Automotive Consumer Goods Electrical/Electronic Applications Hose/Tubing Industrial Applications
| General | |||
| Form | Resin Pellets |
||
| Feature | Medium-Low Viscosity Crystalline | Homopolymer Chemical Resistant |
Excellent Processability Ec 1907/2006 (Reach) |
| Bushings Fittings Furniture | |||
| Uses Electrical Engineering Gear Wheels Electrical | |||
| Valves/Valve Parts | |||
| Physical Nominal Value Test Method | |||
| Density, dry 1.13 g/cm³ ASTM D792;ISO 1183 |
|||
| Dry: Molding Shrinkage - Flow(3.18 mm) 0.90 % No Standard | |||
| Dry: Water Absorption | |||
| 24 hr 1.6 % ASTM D570 | |||
| 24 hr;23 °C 1.6 % ISO 62 | |||
| Dry: Water Absorption, Saturation | |||
| 9.3 % ASTM D570 | |||
| 23 °C 9.3 % ISO 62 | |||
| Dry: Water Absorption, Equilibrium | |||
| 50% RH 2.6 % ASTM D570 | |||
| 50% RH;23 °C 2.6 % ISO 62 | |||
| Dry: Rockwell Hardness, R-Scale 120 ASTM D785 | |||
| Mechanical Nominal Value Test Method | |||
| Dry: Tensile Modulus ISO 527-2 | |||
| -40 °C 4090 MPa | |||
| 23 °C 3700 MPa | |||
| 80 °C 750 MPa | |||
| 120 °C 550 MPa | |||
| 150 °C 445 MPa | |||
| Condition: Tensile Modulus(23 °C) | 1360 MPa | ISO 527-2 |
| Dry: Tensile Strength, Yield -40 °C 80 °C 23 °C 121 °C 23 °C 120 °C 150 °C |
137 MPa 40.0 MPa 90.0 MPa 30.0 MPa 88.0 MPa 30.0 MPa 25.0 MPa |
ASTM D638;ISO 527-2 ASTM D638;ISO 527-2 ASTM D638 ASTM D638 ISO 527-2 ISO 527-2 ISO 527-2 |
| Condition: Tensile Strength, Yield -40 °C 80 °C 23 °C 121 °C 23 °C 120 °C |
142 MPa 30.0 MPa 48.0 MPa 25.0 MPa 43.0 MPa 25.0 MPa |
ASTM D638;ISO 527-2 ASTM D638;ISO 527-2 ASTM D638 ASTM D638 ISO 527-2 ISO 527-2 |
| Dry: Tensile Strength, Break -40 °C 23 °C 80 °C 121 °C |
130 MPa 90.0 MPa 35.0 MPa 25.0 MPa |
ASTM D638 |
| Condition: Tensile Strength, Break -40 °C 23 °C 80 °C 121 °C |
80.0 MPa 70.0 MPa 30.0 MPa 20.0 MPa |
ASTM D638 |
| Dry: Tensile Elongation, Yield -40 °C 80 °C 121 °C 23 °C |
3.0 % 25 % 27 % 4.0 % |
ASTM D638 ASTM D638 ASTM D638 ASTM D638;ISO 527-2 |
| Condition: Tensile Elongation, Yield -40 °C 80 °C 121 °C 23 °C |
3.0 % 25 % 30 % 22 % |
ASTM D638 ASTM D638 ASTM D638 ASTM D638;ISO 527-2 |
| Dry: Tensile Elongation, Break -40 °C 23 °C 80 °C 121 °C |
5.0 % 12 % > 100 % > 100 % |
ASTM D638 |
| Condition: Tensile Elongation, Break -40 °C 23 °C 80 °C 121 °C |
3.0 % > 100 % > 100 % > 100 % |
ASTM D638 |
| Dry: Nominal Tensile Strain at Break -40 °C 23 °C 80 °C 120 °C |
5.0 % 7.0 % > 100 % > 100 % |
ISO 527-2 |
| Condition: Nominal Tensile Strain at Break -40 °C 23 °C 80 °C 120 °C |
3.0 % > 50 % > 100 % > 100 % |
ISO 527-2 |
| Dry: Flexural Modulus -40 °C 23 °C 65 °C 90 °C 121 °C 23 °C |
3370 MPa 3170 MPa 600 MPa 440 MPa 385 MPa 2800 MPa |
ASTM D790 ASTM D790 ASTM D790 ASTM D790 ASTM D790 ISO 178 |
| Condition: Flexural Modulus -40 °C 23 °C |
4200 MPa 970 MPa |
ASTM D790 |
| Dry: Flexural Strength -40 °C 23 °C 65 °C 121 °C 23 °C |
183 MPa 110 MPa 30.0 MPa 21.0 MPa 95.0 MPa |
ASTM D790 ASTM D790 ASTM D790 ASTM D790 ISO 178 |
| Condition: Flexural Strength -40 °C 23 °C |
168 MPa 42.0 MPa |
ASTM D790 |
| Dry: Charpy Notched Impact Strength(23 °C) | 3.5 kJ/m² | ISO 179 |
| Dry: Charpy Unnotched Impact Strength(23 °C) | No Break | ISO 179 |
| Dry: Notched Izod Impact -40 °C 23 °C |
32 J/m 48 J/m |
ASTM D256 |
| Izod Notched Impact: condition -40 °C 23 °C |
21 J/m 170 J/m |
ASTM D256 |
| Dry: Drop Weight Impact Strength(23 °C) | 122 J | Internal Method |
| Thermal | Nominal Value | Test Method |
| Dry: Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa 0.45 MPa 1.8 MPa |
190 °C 75.0 °C 165 °C 65.0 °C |
ASTM D648 ASTM D648 ISO 75-2/B ISO 75-2/A |
| Dry: Peak Melting Temperature | 220 °C | ASTM D3418;ISO 3146 |
| Dry: CLTE - Flow | 8.1E-5 cm/cm/°C | ASTM E831 |
| Dry: RTI Elec 0.71 mm 1.5 mm 3 mm 6 mm |
125 °C 125 °C 125 °C 125 °C |
UL 746 |
| Dry: RTI Imp 0.71 mm 1.5 mm 3 mm 6 mm |
65.0 °C 75.0 °C 75.0 °C 75.0 °C |
UL 746 |
| Dry: RTI Str 0.71 mm 1.5 mm 3 mm 6 mm |
65.0 °C 85.0 °C 85.0 °C 85.0 °C |
UL 746 |
| Dry: Flame Rating 0.71 mm 1.5 mm 3 mm 6 mm |
V-2 V-2 V-2 V-2 |
UL 94 |
| Electrical | Nominal Value | Test Method |
| Dry: Volume Resistivity | ||
| 1.5 mm | > 1.0E+15 Ohms ·cm > 1.0E+15 Ohms ·cm |
ASTM D257 IEC 60093 |
| Dry: Dielectric Strength, Method A, Short-Time(1.5 mm) | 30 kV/mm | ASTM D149 |
| Dry: Comparative Tracking Index | 600 V | IEC 60112 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 80 °C | |
| Drying Time<Injection> | 2.0 - 4.0 hr | |
| Suggested Max Moisture<Injection> | 0.15 % | |
| Processing Temp, Melt<Injection> | 240 - 285 °C | |
| Mold Temperature<Injection> | 65 - 80 °C | |
| Injection Pressure<Injection> | 3.50 - 12.5 MPa | |
| Injection Rate<Injection> | Fast |