Product Description | |||
Polypropylene copolymer reinforced with 15% chemically coupled glass fiber | |||
General | |||
Form | Resin Pellets | ||
Filler | 15 % Glass Fiber | ||
Feature Ec 1907/2006 (Reach) Chemically Coupled | |||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.00 g/cm³ | ASTM D792 | |
Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) | 7.0 g/10min | ASTM D1238 | |
Molding Shrinkage | 1.0 % | ||
Water Absorption(24 hr;23 °C) | 0.020 % | ASTM D570 | |
Ash Content | 15 % | Internal Method | |
Mechanical | Nominal Value | Test Method | |
Tensile Strength, Break | 55.0 MPa | ASTM D638 | |
Flexural Modulus | 3100 MPa | ASTM D790 | |
Flexural Strength | 80.0 MPa | ASTM D790 | |
Charpy Notched Impact Strength(23 °C) | 14 kJ/m² | ISO 179 1eA | |
Notched Izod Impact | ASTM D256 | ||
-20 °C | 130 J/m | ||
23 °C | 160 J/m | ||
Thermal | Nominal Value | Test Method | |
Deflection Temperature Under Load, Unannealed(1.8 MPa) | 130 °C | ASTM D648 | |
CLTE, Flow | 6.5E-5 cm/cm/°C | ASTM D696 | |
Flame Rating(3.2 mm) | HB | UL 94 | |
Electrical | Nominal Value | Test Method | |
Surface Resistivity | 1.0E+15 ohms | ASTM D257 | |
Dielectric Constant(1000000 Hz) | 2.30 | ASTM D150 | |
Comparative Tracking Index | 650 V | IEC 60112 |
Processing | Nominal Value |
Drying Temperature<Injection> | 90 °C |
Drying Time<Injection> | 3.0 hr |
Rear Temperature<Injection> | 210 °C |
Middle Temperature<injection> | 240 °C |
Front Temperature<Injection> | 250 °C |
Mold Temperature<Injection> | 50 - 70 °C |