Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | |||
FXM2143H is a high flow, UV stabilized, high heat polycarbonate copolymer with an HDT/Af of 142 C. | |||
General | |||
Form Resin Pellets | |||
Feature | Excellent Processability Good Thermal Good Surface Appearance | Outdoor | |
Uses Industria | Electrical | ||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.2 1.2 g/cm³ |
ASTM D792 ISO 1183 |
|
Mold Shrinkage, Flow(3.2 mm) | 0.6 - 0.9 % | Method | |
Melt Flow Rate[MFR](330 °C;2.16 kgf) | 46 g/10min | ASTM D1238 | |
Water Absorption(23 °C;saturated) | 0.3 % | ISO 62-1 | |
Moisture Absorption(50% RH;23 °C) | 0.23 % | ISO 62 | |
Melt Volume Rate, MVR(2.16 kg;330 °C) | 43 cm³/10 min | ISO 1133 | |
Mechanical | Nominal Value | Test Method | |
Izod Impact, Notched | |||
23 °C | 115 J/m | ASTM D256 | |
-30 °C | 75 J/m | ASTM D256 | |
80*10*4;23 °C | 11 kJ/m² | ISO 180/1A | |
80*10*4;-30 °C | 10 kJ/m² | ISO 180/1A | |
Instrumented Dart Impact, Total Energy(23 °C) | 68 J | ASTM D3763 | |
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 20 kJ/m² | ISO 179 1eA | |
Tensile Stress, Yield | |||
50 mm/min;Type I | 70 MPa | ASTM D638 | |
50 mm/min | 70 MPa | ISO 527 | |
Tensile Stress, Break | |||
50 mm/min;Type I | 60 MPa | ASTM D638 | |
50 mm/min | 60 MPa | ISO 527 | |
Tensile Strain, Yield | |||
50 mm/min;Type I | 6.5 % | ASTM D638 | |
50 mm/min | 6.5 % | ISO 527 | |
Tensile Strain, Break | |||
50 mm/min;Type I | 90 % | ASTM D638 | |
50 mm/min | 90 % | ISO 527 | |
Tensile Modulus | |||
5 mm/min | 2600 MPa | ASTM D638 | |
1 mm/min | 2600 MPa | ISO 527 | |
Flexural Stress, Yield | |||
1.3 mm/min;50 mm;span | 110 MPa | ASTM D790 | |
2 mm/min | 100 MPa | ISO 178 | |
Flexural Modulus | |||
1.3 mm/min;50 mm;span | 2550 MPa | ASTM D790 | |
2 mm/min | 2450 MPa | ISO 178 | |
Thermal | Nominal Value | Test Method | |
Vicat Softening Temperature | |||
Rate B/50 | 161 °C | ASTM D1525 | |
Rate B/50 | 160 °C | ISO 306 | |
Rate B/120 | 162 °C | ISO 306 | |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
155 °C 145 °C |
ASTM D648 | |
CTE, Flow | |||
-40 - 40 °C | 6.0E-05 1/°C | ASTM E831 | |
-40 - 40 °C | 6.0E-05 1/°C | ISO 11359-2 | |
CTE, XFlow | |||
-40 - 40 °C | 6.0E-05 1/°C | ASTM E831 | |
-40 - 40 °C | 6.0E-05 1/°C | ISO 11359-2 | |
HDT/Af(1.8) | 142 °C | ISO 75/Af | |
Processing | Nominal Value | ||
Drying Temperature<Injection> | 125 °C | ||
Drying Time<Injection> | 4 - 6 hrs | ||
Maximum Moisture Content<Injection> | 0.02 % | ||
Melt Temperature<Injection> | 290 - 330 °C | ||
Nozzle Temperature<Injection> | 285 - 330 °C | ||
Front, Zone 3 Temperature<Injection> | 290 - 330 °C | ||
Middle, Zone 2 Temperature<Injection> | 280 - 320 °C | ||
Rear, Zone 1 Temperature<Injection> | 270 - 300 °C | ||
Mold Temperature<Injection> | 85 - 130 °C | ||
Back Pressure<Injection> | 0.3 - 0.7 MPa | ||
Screw Speed <Injection> | 40 - 90 rpm | ||
Shot To Cylinder Size<Injection> | 40 - 60 % | ||
Vent Depth <Injection> | 0.025 - 0.08 mm |