LNP ELCRES DMX1435D is a UV stabilized standard flow Polycarbonate (PC) copolymer resin with diffusion effect and improved scratch resistance. This grade is a good candidate for consumer electronics, mobility interiors and other adjacent applications, which need lower scratch and diffusive effects performance.
Product Description | |||
LNP ELCRES DMX1435D is a UV stabilized standard flow Polycarbonate (PC) copolymer resin with diffusion effect and improved scratch resistance. This grade is a good candidate for consumer electronics, mobility interiors and other adjacent applications, which need lower scratch and diffusive effects performance. | |||
General | |||
Form | Resin Pellets | ||
Feature Diffusive Anti-Scratch Outdoor | |||
Automotive Consumer Building and Construction |
Electrical | ||
Physical | Nominal Value | Test Method | |
Specific Gravity | 1.18 | ASTM D792 | |
Specific Volume | 0.85 cm³/g | ASTM D792 | |
Density | 1.17 g/cm³ 1.18 g/cm³ |
ASTM D792 ISO 1183 |
|
Water Absorption 24 hrs;23 °C 23°C/Saturated 23 °C;saturated |
0.08 % 0.28 % 0.27 % |
ASTM D570 ASTM D570 ISO 62-1 |
|
Moisture Absorption, Equilibrium(50% RH) | 0.13 % | ASTM D570 | |
Moisture Absorption 23 °C;50% RH/24 hrs 50% RH;23 °C |
0.04 % 0.13 % |
ASTM D570 ISO 62 |
|
Mold Shrinkage, Flow(3.2 mm) | 0.5 - 0.8 % | SABIC Method | |
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 15.4 g/10min | ASTM D1238 | |
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 14 cm³/10 min | ISO 1133 | |
Mechanical | Nominal Value | Test Method | |
Izod Impact, Unnotched(23 °C) | NB J/m | ASTM D4812 | |
Izod Impact, Notched | ASTM D256 | ||
23 °C | 30 J/m | ||
-30 °C | 30 J/m | ||
Instrumented Dart Impact, Total Energy(23 °C) | 7 J | ASTM D3763 |
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 |
NB kJ/m² 40 kJ/m² |
ISO 180/1U |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
2.2 kJ/m² 2 kJ/m² |
ISO 180/1A |
Charpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
2.2 kJ/m² 2.5 kJ/m² |
ISO 179 1eA |
Charpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
NB kJ/m² 46 KJ/m² |
ISO 179 1eU |
Tensile Stress, Yield 50 mm/min;Type I 50 mm/min |
77 MPa 77 MPa |
ASTM D638 ISO 527 |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
60 MPa 59 MPa |
ASTM D638 ISO 527 |
Tensile Strain, Yield 50 mm/min;Type I 50 mm/min |
7.5 % 7 % |
ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
20 % 20 % |
ASTM D638 ISO 527 |
Tensile Modulus 50 mm/min 1 mm/min |
2700 MPa 2400 MPa |
ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min |
120 MPa 110 MPa |
ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2500 MPa 2600 MPa |
ASTM D790 ISO 178 |
Hardness, Rockwell L | 110 | ASTM D785 |
Hardness, Rockwell M | 90 | ASTM D785 |
Pencil Hardness Test(1kgf) | H | ASTM D3363 |
Thermal | Nominal Value | Test Method |
UL Recognized(≥ 0.6 mm) | HB | UL 94 |
Vicat Softening Temperature | ||
Rate B/50 | 138 °C | ASTM D1525 |
Rate B/50 | 136 °C | ISO 306 |
Rate B/120 | 138 °C | ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
129 °C 115 °C |
ASTM D648 |
CTE, Flow -40°C to 95°C 23°C to 80°C |
7.0E-05 1/°C 7.0E-05 1/°C |
ASTM E831 ISO 11359-2 |
CTE, XFlow -40°C to 95°C 23°C to 80°C |
7.0E-05 1/°C 7.0E-05 1/°C |
ASTM E831 ISO 11359-2 |
HDT/Bf(0.45) | 129 °C | ISO 75/Bf |
HDT/Af(1.8) | 115 °C | ISO 75/Af |
Relative Temp Index, Elec | 80 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 80 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 80 °C | UL 746B |
Optical | Nominal Value | Test Method |
Light Transmission At 2.0 Mm(2 mm) | 85 % | ASTM D1003 |
Haze(2 mm) | 85 % | SABIC Method |
Processing | Nominal Value |
Drying Temperature<Injection> | 120 °C |
Drying Time<Injection> | 3 - 4 hrs |
Maximum Moisture Content<Injection> | 0.02 % |
Melt Temperature<Injection> | 295 - 315 °C |
Nozzle Temperature<Injection> | 290 - 310 °C |
Front, Zone 3 Temperature<Injection> | 295 - 315 °C |
Middle, Zone 2 Temperature<Injection> | 280 - 305 °C |
Rear, Zone 1 Temperature<Injection> | 260 - 280 °C |
Hopper Temperature<Injection> | 60 - 80 °C |
Mold Temperature<Injection> | 70 - 95 °C |