a-1145 HS Is Heat Stabilized Polyphthalamide (PPA) with a High Heat Deflection Temperature

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PPA-A-1145HS
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Resin Pellets PPA with 45 % Glass Fiber for High Mechanical Strength And Rigidity
 Heat-conducting nylon

Product Description

Product Description
A-1145 HS is a 45% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, very high flexural modulus and very high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. Black: A-1145 HS BK 324 Natural: A-1145 HS NT
General
Form		Resin Pellets
Filler		45 % Glass Fiber
Feature
		Good Dimensional		Enhanced Stiffness           Low Moisture
UL Yellow Card                         E95746-253218
Automotive Electronics      Automotive Under The     Industrial Applications
oo                                   Industrial Parts
Housing                             Power                                Valves/Valve Parts
Mechanical Parts
Physical                                                                                 Nominal Value                                       Test Method
Density, dry                                                                           1.59 g/cm³                                             ISO 1183/A
Dry: Molding Shrinkage, Flow                                             0.20 %                                                     ASTM D955
Condition: Molding Shrinkage, Flow                                  0.10 %                                                     ASTM D955
Dry: Molding Shrinkage, Across Flow                                 0.60 %                                                     ASTM D955
Condition: Molding Shrinkage, Across Flow                      0.10 %                                                    ASTM D955
Dry: Water Absorption(24 hr)                                              0.12 %                                                    ASTM D570
Dry: Rockwell Hardness, R-Scale                                         125                                                          ASTM D785
Mechanical                                                                            Nominal Value                                      Test Method
Dry: Tensile Modulus
17200 MPa                                            ASTM D638
23 °C                                                                                     16800 MPa                                             ISO 527-2
100 °C                                                                                  11200 MPa                                              ISO 527-2
150 °C                                                                                  8000 MPa                                                ISO 527-2
175 °C                                                                                   5380 MPa                                               ISO 527-2
Condition: Tensile Modulus                                                17200 MPa                                             ASTM D638
Dry: Tensile Stress, Break 23 °C 100 °C 150 °C 175 °C			263 MPa 173 MPa 84.8 MPa 75.8 MPa		ISO 527-2
Dry: Tensile Stress			259 MPa		ASTM D638
Condition: Tensile Stress			228 MPa		ASTM D638
Dry: Tensile Elongation, Break
			2.6 %		ASTM D638
23 °C			2.7 %		ISO 527-2
100 °C			2.5 %		ISO 527-2
150 °C			7.2 %		ISO 527-2
175 °C			6.5 %		ISO 527-2
Condition: Tensile Elongation, Break			2.1 %		ASTM D638
Dry: Flexural Modulus
			13800 MPa		ASTM D790
23 °C			15900 MPa		ISO 178
100 °C			13000 MPa		ISO 178
150 °C			5380 MPa		ISO 178
175 °C			4900 MPa		ISO 178
Condition: Flexural Modulus			13800 MPa		ASTM D790
Dry: Flexural Strength
			363 MPa		ASTM D790
23 °C			377 MPa		ISO 178
100 °C			267 MPa		ISO 178
150 °C			111 MPa		ISO 178
175 °C			94.5 MPa		ISO 178
Condition: Flexural Strength			294 MPa		ASTM D790
Dry: Compressive Strength(25.4 mm)			194 MPa		ASTM D695
Dry: Shear Strength			108 MPa		ASTM D732
Condition: Shear Strength			91.7 MPa		ASTM D732
Dry: Poisson's Ratio			0.41		ASTM E132
Dry: Charpy Notched Impact Strength(23 °C)			10 kJ/m²		ISO 179 1eA
Dry: Charpy Unnotched Impact Strength(23 °C)			92 kJ/m²		ISO 179 1eU
Dry: Notched Izod Impact 23 °C			110 J/m 10 kJ/m²		ASTM D256 ISO 180/1A
Izod Notched Impact: condition			100 J/m		ASTM D256
Dry: Unnotched Izod Impact 23 °C			1100 J/m 61 kJ/m²		ASTM D256 ISO 180/1U
Thermal			Nominal Value		Test Method
Dry: Deflection Temperature Under Load, Annealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm			301 °C 287 °C		ASTM D648
Dry: Deflection Temperature Under Load, Unannealed(1 8 MPa)			281 °C		ISO 75-2/A
Dry: Continuous Use Temperature 2.0e+4 hr 5.0e+3 hr			165 °C 185 °C		ASTM D3045
Dry: Melting Temperature			310 °C		ASTM D3418;ISO 11357-3
Dry: CLTE, Flow 0 - 100 °C 100 - 200 °C			1.4E-5 cm/cm/°C 3.5E-5 cm/cm/°C		ASTM E831
Dry: CLTE, Transverse 0 - 100 °C 100 - 200 °C			5.0E-5 cm/cm/°C 1.5E-4 cm/cm/°C		ASTM E831
Dry: Flame Rating(3.2 mm)			HB		UL 94
Electrical			Nominal Value		Test Method
Dry: Volume Resistivity			1.0E+16 ohms ·cm		ASTM D257
Condition: Volume resistivity			2.0E+15 ohms ·cm		ASTM D257
Dry: Dielectric Strength(3.2 mm)			23 kV/mm		ASTM D149
Condition: Dielectric Strength(3.2 mm)			23 kV/mm		ASTM D149
Dry: Dielectric Constant 60 Hz 1.0e+6 Hz			4.60 4.40		ASTM D150
Condition: Dielectric Constant 60 Hz 1.0e+6 Hz			4.90 4.50		ASTM D150
Dry: Dissipation Factor 60 Hz 1.0e+6 Hz			5.0E-3 0.016		ASTM D150
Condition: Dissipation factor 60 Hz 1.0e+6 Hz			9.0E-3 0.021		ASTM D150
Dry: Arc Resistance			145 sec		ASTM D495
Condition: Arc Resistance			125 sec		ASTM D495
Dry: Comparative Tracking Index, CTI			550 V		UL 746
Condition: Comparative Tracking Index, CTI			550 V		UL 746
Processing					Nominal Value
Drying Temperature<Injection>					120 °C
Drying Time<Injection>					4.5 hr
Suggested Max Moisture<Injection>					0.030 - 0.060 %
Rear Temperature<Injection>					304 - 318 °C
Front Temperature<Injection>					316 - 329 °C
Processing Temp, Melt<Injection>					321 - 343 °C
Mold Temperature<Injection>					135 °C

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 