Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | |
Global grade. LEXAN XLS1110 is an injection molding grade especially designed for manufacturing optical parts requiring excellent flow properties combined with very high transmission and color stability. | |
General | |
Form Resin Pellets | |
Feature High Clarity | |
Uses Automotive Lighting Optical Applications | |
Physical Nominal Value Test Method | |
Density / Specific Gravity 1.20 g/cm³ ISO 1183 | |
Melt Volume-Flow Rate, MVR ISO 1133 | |
250 °C;1.2 kg 6.00 cm³/10 min | |
300 °C;1.2 kg 35 cm³/10 min | |
Molding Shrinkage, Flow, Tensile Bar 0.50 - 0.70 % | ASTM D792;ISO 1183 |
Water Absorption, Saturation(23 °C) 0.35 % | ASTM D1895;ISO 60 |
Water Absorption, Equilibrium(50% RH;23 °C) 0.15 % | ASTM D1238;ISO 1133 |
Ball Indentation Hardness(H 358/30) 95.0 MPa ISO 2039-1 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | 2350 MPa | ISO 527-2/1 |
Tensile Stress, Yield | 61.0 MPa | ISO 527-2/50 |
Tensile Stress, Break | 64.0 MPa | ISO 527-2/50 |
Tensile Strain, Yield | 6.0 % | ISO 527-2/50 |
Tensile Strain, Break | 75 % | ISO 527-2/50 |
Flexural Modulus(2 mm/min) | 2300 MPa | ISO 178 |
Flexural Stress, at Yield(2 mm/min) | 90.0 MPa | ISO 178 |
Taber Abrasion Resistance(1.0e+3 Cycles;1.0e+3 Wheel) | g;CS-1710.0 mg | Internal Method |
C harpy Notched Impact Strength -30 °C;80 23 °C;80 |
11 kJ/m² 55 kJ/m² |
ISO 179 1eA |
C harpy Unnotched Impact Strength -30 °C;80 23 °C;80 |
No Break No Break |
ISO 179 1eU |
Notched Izod Impact Strength -30 °C;80*10*3 mm 23 °C;80*10*3 mm |
14 kJ/m² 57 kJ/m² |
ISO 180/1A |
Unnotched Izod Impact Strength -30 °C;80*10*3 mm 23 °C;80*10*3 mm |
No Break No Break |
ISO 180/1U |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed 0.45 MPa;120*10*4 mm;4 mm;100 mm;Span 1.8 MPa;120*10*4 mm;4 mm;100 mm;Span |
133 °C 122 °C |
ISO 75-2/Be ISO 75-2/Ae |
Vicat Softening Temperature | 144 °C 145 °C |
ISO 306/B50 ISO 306/B120 |
Ball Pressure Test(123 - 127 °C) | Pass | IEC 60695-10-2 |
CLTE, Flow(23 - 80 °C) | 7.0E-5 cm/cm/°C | ISO 11359-2 |
Thermal Conductivity | 0.20 W/m-K | ISO 8302 |
RTI Elec | 130 °C | UL 746 |
RTI Imp | 125 °C | UL 746 |
RTI Str | 125 °C | UL 746 |
Glow Wire Flammability Index(1 mm) | 850 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT](1 mm) | > 875 °C | IEC 60695-2-13 |
Oxygen Index | 25 % | ISO 4589-2 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 |
Volume Resistivity | > 1.0E+15 Ohms ·cm | IEC 60093 |
Electric Strength, in Oil(3.2 mm) | 17 kV/mm | IEC 60243-1 |
Relative Permittivity 50 Hz 60 Hz 1.0e+6 Hz |
2.70 2.70 2.70 |
IEC 60250 |
Dissipation Factor 50 Hz 60 Hz 1.0e+6 Hz |
1.0E-3 1.0E-3 0.010 |
IEC 60250 |
Comparative Tracking Index | 250 V | IEC 60112 |
Optical | Nominal Value | Test Method |
Refractive Index | 1.586 | ISO 489 |
Transmittance | ||
2.5e+3 µm | > 90.0 % | ASTM D1003 |
2.5e+3 µm;420 nm | > 88.0 % | Internal Method |
5.0e+3 µm | > 89.0 % | Internal Method |
Haze(2.5e+3 µm) | < 0.500 % | ASTM D1003 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Rear Temperature<Injection> | 260 - 280 °C | |
Middle Temperature<injection> | 270 - 290 °C | |
Front Temperature<Injection> | 280 - 300 °C | |
Nozzle Temperature<Injection> | 270 - 290 °C | |
Processing Temp, Melt<Injection> | 280 - 300 °C | |
Mold Temperature<Injection> | 80 - 100 °C |