Feature: | Oxidative Degradable |
---|---|
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Light Diffusion, Medium class
Product Description | |||
Light Diffusion, Medium class | |||
General | |||
Form | Resin Pellets | ||
Feature | Diffusive | ||
Lighting Applications Lighting Diffusers Displays Led |
|||
Physical | Nominal Value | Test Method | |
Density | 1.20 g/cm³ | ISO 1183 | |
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 20 g/10min | ISO 1133 | |
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) | 20 cm³/10 min | ISO 1133 | |
Molding Shrinkage, Across Flow | 0.50 - 0.70 % | Internal Method | |
Molding Shrinkage, Flow | 0.50 - 0.70 % | Internal Method | |
Water Absorption, Saturation(23 °C) | 0.24 % | ISO 62 | |
Mechanical | Nominal Value | Test Method | |
Tensile Modulus | 2500 MPa | ISO 527-2/1 | |
Tensile Stress, Yield | 63.0 MPa | ISO 527-2/50 | |
Tensile Strain, Yield | 6.0 % | ISO 527-2/50 | |
Nominal Tensile Strain at Break | 110 % | ISO 527-2/50 | |
Flexural Modulus(2 mm/min) | 2400 MPa | ISO 178 | |
Flexural Stress(2 mm/min) | 96.0 MPa | ISO 178 | |
Charpy Notched Impact Strength(23 °C) | 40 kJ/m² | ISO 179 | |
Charpy Unnotched Impact Strength(23 °C) | No Break | ISO 179 | |
Thermal | Nominal Value | Test Method | |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
136 °C 122 °C |
ISO 75-2/B ISO 75-2/A |
|
CLTE, Flow | 6.5E-5 cm/cm/°C | ISO 11359-2 | |
CLTE, Transverse | 6.6E-5 cm/cm/°C | ISO 11359-2 | |
Flame Rating(0.4 mm) | V-2 | UL 94 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 6.0E+15 ohms | IEC 60093 |
Volume Resistivity | 3.0E+16 ohms·cm | IEC 60093 |
CTI | PLC 3 | UL 746 |
Processing | Nominal Value | |
Drying Temperature - Hot Air Dryer<Injection> | 120 °C | |
Drying Time - Hot Air Dryer<Injection> | 4.0 - 8.0 hr | |
Rear Temperature<Injection> | 270 - 300 °C | |
Middle Temperature<injection> | 270 - 300 °C | |
Front Temperature<Injection> | 270 - 300 °C | |
Nozzle Temperature<Injection> | 270 - 300 °C | |
Mold Temperature<Injection> | 70 - 100 °C |