| LNP THERMOCOMP MF002S compound is based on Polypropylene (PP) resin containing 10% glass fiber. Added features of this grade include: Heat Stabilized. | ||||
| General | ||||
| Form Resin Pellets | ||||
| Filler 10 % Glass Fiber | ||||
| Feature Good Thermal Good Hardness Structural | ||||
| Uses Consumer Electrical | ||||
| Physical Nominal Value Test Method | ||||
| Density / Specific Gravity 0.97 0.96 g/cm³ |
ASTM D792 | |||
| Mold Shrinkage, Flow(24 hrs) 1 - 3 % ASTM D955 | ||||
| Mold Shrinkage, XFlow(24 hrs) 1 - 3 % ASTM D955 | ||||
| Moisture Absorption(50% RH;23 °C) 1.0E-02 % ISO 62 | ||||
| Mechanical | Nominal Value | Test Method | ||
| Izod Impact, Unnotched | ||||
| 23 °C | 488 J/m | ASTM D4812 | ||
| 80*10*4;23 °C | 29 kJ/m² | ISO 180/1U | ||
| Izod Impact, Notched | ||||
| 23 °C | 38 J/m | ASTM D256 | ||
| 80*10*4;23 °C | 5 kJ/m² | ISO 180/1A | ||
| Multiaxial Impact | 1 J | ISO 6603 | ||
| Instrumented Dart Impact, Total Energy(23 °C) | 4 J | ASTM D3763 | ||
| Tensile Stress, Yield | ||||
| 5 mm/min;Type I | 46 MPa | ASTM D638 | ||
| 5 mm/min | 46 MPa | ISO 527 | ||
| Tensile Stress, Break | ||||
| 5 mm/min;Type I | 42 MPa | ASTM D638 | ||
| 5 mm/min | 44 MPa | ISO 527 | ||
| Tensile Strain, Yield | ||||
| 5 mm/min;Type I | 4.7 % | ASTM D638 | ||
| 5 mm/min | 4.4 % | ISO 527 | ||
| Tensile Strain, Break | ||||
| 5 mm/min;Type I | 6.7 % | ASTM D638 | ||
| 5 mm/min | 5.8 % | ISO 527 | ||
| Tensile Modulus | ||||
| 50 mm/min | 2980 MPa | ASTM D638 | ||
| 1 mm/min | 2970 MPa | ISO 527 | ||
| Flexural Stress | ||||
| 75 MPa | ASTM D790 | |||
| 64 MPa | ISO 178 | |||
| Flexural Modulus | ||||
| 1.3 mm/min;50 mm;span | 2390 MPa | ASTM D790 | ||
| 2 mm/min | 2330 MPa | ISO 178 | ||
| Thermal | Nominal Value | Test Method | ||
| UL Recognized(≥ 1 mm) | HB | UL 94 | ||
| Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm |
875 °C 850 °C |
IEC 60695-2-13 | ||
| Glow Wire Flammability Index 3 mm 1.5 mm |
850 °C 850 °C |
IEC 60695-2-12 | ||
| Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
154 °C 113 °C |
ASTM D648 | ||
| CTE, Flow(-30 - 30 °C) | 6.6E-05 1/°C | ASTM D696 | ||
| CTE, XFlow(-30 - 30 °C) | 8.8E-05 1/°C | ASTM D696 | ||
| HDT/Bf(0.45) | 146 °C | ISO 75/Bf | ||
| HDT/Af(1.8) | 99 °C | ISO 75/Af | ||
| Relative Temp Index, Elec | 65 °C | UL 746B | ||
| Relative Temp Index, Mechanical with Impact | 65 °C | UL 746B | ||
| Relative Temp Index, Mechanical without Impact | 65 °C | UL 746B | ||
| Electrical | Nominal Value | Test Method | ||
| Comparative Tracking Index, CTI | PLC 0 | UL 746A | ||
| Hot-wire Ignition, HWI ≥ 3 mm ≥ 1 mm |
PLC 2 PLC 3 |
UL 746A | ||
| High Amp Arc Ignition, HAI ≥ 1.5 mm ≥ 1 mm |
PLC 1 PLC 3 |
UL 746A | ||
| High Voltage Arc Tracking Rate, HVTR | PLC 1 | UL 746A | ||
| Arc Resistance, Tungsten Electrode | PLC 6 | ASTM D495 | ||
| Processing | Nominal Value | |||
| Drying Temperature<Injection> | 80 °C | |||
| Drying Time<Injection> | 4 hrs | |||
| Melt Temperature<Injection> | 225 - 250 °C | |||
| Front, Zone 3 Temperature<Injection> | 240 - 250 °C | |||
| Middle, Zone 2 Temperature<Injection> | 215 - 225 °C | |||
| Rear, Zone 1 Temperature<Injection> | 195 - 205 °C | |||
| Mold Temperature<Injection> | 30 - 50 °C | |||
| Back Pressure<Injection> | 0.2 - 0.3 MPa | |||
| Screw Speed <Injection> | 30 - 60 rpm | |||