Product Description |
Injection Molding grade, Light diffusion grade, Weather resistance |
General |
Form Resin Pellets |
Feature Diffusive Outdoor |
Uses Lighting Applications Lighting Diffusers Led |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.22 g/cm³ ISO 1183 |
Melt volume-flow rate(300 °C;1.2 kg) 18 cm³/10 min ISO 1133 |
Molding Shrinkage, Across Flow(4 mm) 0.50 - 0.70 % Internal Method |
Molding Shrinkage, Flow(4 mm) 0.50 - 0.70 % Internal Method |
Mechanical Nominal Value Test Method |
Tensile Stress, Yield 61.0 MPa ISO 527-2/50 |
Tensile Stress, Break 60.0 MPa ISO 527-2/50 |
Tensile Strain, Break 90 % ISO 527-2/50 |
Flexural Modulus(2 mm/min) 2150 MPa ISO 178 |
Flexural Stress(2 mm/min) 95.0 MPa ISO 178 |
C harpy Notched Impact Strength(23 °C) 10 kJ/m² ISO 179 |
Thermal Nominal Value Test Method |
Heat Deflection Temperature, Unannealed(1.8 MPa) 126 °C ISO 75-2/A |
CLTE, Flow 7.0E-5 cm/cm/°C ISO 11359-2 |
CLTE, Transverse 7.0E-5 cm/cm/°C ISO 11359-2 |
RTI Elec(0.75 mm) 125 °C UL 746B |
RTI Imp(0.75 mm) 115 °C UL 746B |
RTI Str(0.75 mm) 125 °C UL 746B |
Flame Rating(0.4 mm) V-2 UL 94 |
Electrical Nominal Value Test Method |
Surface Resistivity > 1.0E+15 Ohms IEC 60093 |
Volume Resistivity > 1.0E+15 Ohms ·cm IEC 60093 |
Optical Nominal Value Test Method |
Light Transmission JIS K7361 |
1.0e+3 µm 68.0 % |
2.0e+3 µm 55.0 % |
Processing |
Nominal Value |
Drying Temperature |
120 °C |
Drying Time |
5.0 - 8.0 hr |
Processing Temp, Melt |
270 - 320 °C |
Mold Temperature |
80 - 120 °C |