PA66 grade for machinery components high stiffness and dimensional stability
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | ||||||||||
A3EG7 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. Applications Typical applications include lamp socket housings, cooling fans, insulating profile for aluminium window frames, water containers for automotive cooling systems, as well as electrically insulating parts. |
||||||||||
General | ||||||||||
Form | Resin Pellets | |||||||||
Filler | 35 % Glass Fiber | |||||||||
Feature | Good Dimensional Ec 1907/2006 (Reach) |
Good Hardness | Fuel Resistant | |||||||
UL Yellow Card | E41871-233731 | |||||||||
Uses | Automotive Containers |
Electrical Engineering Mechanical Parts | Housing | |||||||
Physical | Nominal Value | Test Method | ||||||||
Density, dry | 1.41 g/cm³ | ASTM D792;ISO 1183 | ||||||||
Dry: Melt Volume-Flow Rate, MVR(275 °C;5 kg) | 40 cm³/10 min | ISO 1133 | ||||||||
Dry: Molding Shrinkage - Flow(3.18 mm) | 0.30 % | No Standard | ||||||||
Dry: Water Absorption, Saturation | ||||||||||
5.0 % | ASTM D570 | |||||||||
23 °C | 5.0 % | ISO 62 | ||||||||
Dry: Water Absorption, Equilibrium | ||||||||||
50% RH | 1.6 % | ASTM D570 | ||||||||
50% RH;23 °C | 1.6 % | ISO 62 | ||||||||
Mechanical | Nominal Value | Test Method | ||||||||
Dry: Tensile Modulus(23 °C) | 11500 MPa | ISO 527-2 | ||||||||
Condition: Tensile Modulus(23 °C) | 8500 MPa | ISO 527-2 | ||||||||
Dry: Tensile Strength, Break | ||||||||||
23 °C | 207 MPa | ASTM D638 | ||||||||
23 °C | 210 MPa | ISO 527-2 | ||||||||
80 °C | 122 MPa | ISO 527-2 | ||||||||
Condition: Tensile Strength, Break(23 °C) | 150 MPa | ISO 527-2 | ||||||||
Dry: Tensile Elongation, Break | ||||||||||
23 °C | 3.0 % | ASTM D638 | ||||||||
23 °C | 3.0 % | ISO 527-2 | ||||||||
80 °C | 5.3 % | ISO 527-2 | ||||||||
Condition: Tensile Elongation, Break(23 °C) | 5.0 % | ISO 527-2 | ||||||||
Dry: Flexural Modulus | ||||||||||
23 °C | 9860 MPa | ASTM D790 | ||||||||
23 °C | 10000 MPa | ISO 178 | ||||||||
Condition: Flexural Modulus(23 °C) | 8480 MPa | ISO 178 | ||||||||
Dry: Charpy Notched Impact Strength -30 °C 23 °C |
12 kJ/m² 14 kJ/m² |
ISO 179 | ||||||||
Condition: Charpy Notched Impact Strength(23 °C) | 22 kJ/m² | ISO 179 | ||||||||
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
75 kJ/m² 95 kJ/m² |
ISO 179 | ||||||||
Condition: Charpy Unnotched Impact Strength(23 °C) | 110 kJ/m² | ISO 179 | ||||||||
Dry: Notched Izod Impact | ||||||||||
-40 °C | 96 J/m | ASTM D256 | ||||||||
23 °C | 120 J/m | ASTM D256 | ||||||||
23 °C | 14 kJ/m² | ISO 180 | ||||||||
Thermal | Nominal Value | Test Method | ||||||||
Dry: Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
250 °C 250 °C |
ISO 75-2/B;ASTM D648 ISO 75-2/A;ASTM D648 |
||||||||
Dry: Peak Melting Temperature | 260 °C | ASTM D3418;ISO 3146 | ||||||||
Dry: CLTE, Flow | 1.0E-5 cm/cm/°C 1.7E-5 cm/cm/°C |
ASTM E831 No Standard |
||||||||
Dry: CLTE, Transverse | 6.5E-5 cm/cm/°C | No Standard | ||||||||
Dry: RTI Elec 0.75 mm 1.5 mm 3 mm 6 mm |
120 °C 120 °C 120 °C 120 °C |
UL 746 | ||||||||
Dry: RTI Imp 1.5 mm 3 mm 6 mm |
120 °C 120 °C 120 °C |
UL 746 | ||||||||
Dry: RTI Str 1.5 mm 3 mm 6 mm |
130 °C 130 °C 130 °C |
UL 746 | ||||||||
Dry: Flame Rating 1.5 mm 3 mm 6 mm |
HB HB HB |
UL 94 | ||||||||
Electrical Nominal Value Test Method | ||||||||||
Dry: Volume Resistivity | ||||||||||
1.5 mm 1.0e+15 ohms ·cm ASTM D257 | ||||||||||
1.0e+15 ohms ·cm IEC 60093 | ||||||||||
Condition: Volume resistivity | ||||||||||
1.5 mm 1.0E+12 ohms ·cm ASTM D257 | ||||||||||
1.0E+12 ohms ·cm IEC 60093 | ||||||||||
Dry: Dielectric Constant(1.0e+6 Hz) 3.50 IEC 60250 | ||||||||||
Condition: Dielectric Constant(1.0e+6 Hz) 5.50 IEC 60250 | ||||||||||
Dry: Dissipation Factor IEC 60250 | ||||||||||
100 Hz 0.020 | ||||||||||
1.0e+6 Hz 0.020 | ||||||||||
Condition: Dissipation factor IEC 60250 | ||||||||||
100 Hz 0.30 | ||||||||||
1.0e+6 Hz 0.15 | ||||||||||
Dry: Comparative Tracking Index 550 V IEC 60112 | ||||||||||
Condition: Comparative Tracking Index 550 V IEC 60112 | ||||||||||
Processing Nominal Value | ||||||||||
Drying Temperature<Injection> 80 °C | ||||||||||
Drying Time<Injection> 2.0 - 4.0 hr | ||||||||||
Suggested Max Moisture<Injection> 0.15 % | ||||||||||
Processing Temp, Melt<Injection> 280 - 305 °C | ||||||||||
Mold Temperature<Injection> 80 - 90 °C | ||||||||||
Injection Pressure<Injection> 3.50 - 12.5 MPa | ||||||||||
Injection Rate<Injection> Fast |