PPA 35% Glass Reinforced Heat Stabilized Lubricated High Performance Polyamide Resin

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PPA-52G35HSL 010 NC
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

PPA 35% glass reinforced heat stabilized lubricated high performance polyamide resin
 Heat-conducting nylon

Product Description

Product Description
HTN52G35HSL NC010 is a 35% glass reinforced, heat stabilized, lubricated high performance polyamide resin that can be molded in water heated molds.Information provided by Performance Polymers
General
Form                                        Resin Pellets
Filler                                         35 % Glass Fiber
Physical		Nominal Value	Test Method
Density / Specific Gravity
DAM		1.47 g/cm³	ASTM D792
DAM		1.45 g/cm³	ISO 1183
Filler Content(DAM)		35 %
Linear Mold Shrinkage
Thickness; 1.6 mm;Flow;DAM		0.25 %
Thickness; 3.2 mm;Flow;DAM		0.3 %
Thickness; 1.6 mm;DAM;Transverse		1 %
Thickness; 3.2 mm;DAM;Transverse		1 %
Linear Mold Shrinkage, Flow(Thickness; 2 mm;DAM)		0.2 %	ISO 294-4
Hardness, Rockwell M		105	ASTM D785
Hardness, Rockwell R		124	ASTM D785
Mechanical		Nominal Value	Test Method
Tensile Strength, Break			ISO 527
Temperature; 23 °C		180 MPa
Temperature; 23 °C		200 MPa
Tensile Strength			ASTM D638
200 °C		72.4 MPa
175 °C		80.0 MPa
150 °C		89.0 MPa
Temperature; 100 °C		124 MPa
Temperature; 23 °C		168 MPa
60 °C		188 MPa
Temperature; 23 °C		204 MPa
Temperature; -40 °C		230 MPa
	Temperature; 150 °C;Strain 0.51 % Temperature; 0 °C;Strain 0.21 %	23.46 MPa 24.31MPa
	40 °C;Strain 0.22 %	24.56 MPa
	Strain 0.2 %;Temperature; -20 °C	24.63 MPa
	Temperature; -20 °C;Strain 0.21 %	25.85 MPa
	Temperature; 120 °C;Strain 0.51 %	26.02 MPa
	Temperature; 0 °C;Strain 0.23 %	26.87 MPa
	Temperature; 150 °C;Strain 0.52 %	27.0 MPa
	Temperature; 60 °C;Strain 0.27 %	29.31 MPa
	Temperature; 23 °C;Strain 0.26 %	29.53 MPa
	90 °C;Strain 0.52 %	30.36 MPa
	Strain 0.48 %;Temperature; 120 °C	31.33 MPa
	90 °C;Strain 0.43 %	33.66 MPa

Comparative Tracking Index
Temperature; 23 °C;DAM	> = 600 V	ASTM D3638
Temperature; 23 °C;DAM	600 V	UL 746A
Temperature; 23 °C;DAM	600 V	IEC 60112
Processing		Nominal Value
Melt Temperature		325 °C 320 - 330 °C
Mold Temperature		95.0 °C 85.0 - 105 °C
Drying Temperature		100 °C
Dry Time		6.00 - 8.00 hour
Moisture Content		< = 0.10 %

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 