Product Description |
Starflam P10003 is a Mineral Flame Retardant, Halogen Free, Red Phosphorous Free, Polyamide 6 Injection Molding Resin |
General |
Form Resin Pellets |
Filler Mineral |
|
Feature Chlorinated Flame |
Retardant |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.50 g/cm³ ISO 1183 |
Molding Shrinkage, Flow(4 mm) 1.0 % Internal Method |
Water Absorption(24 hr;23 °C) 0.90 % ISO 62 |
Mechanical Nominal Value Test Method |
Tensile Modulus 6700 MPa ISO 527-2/1 |
Tensile Stress, Yield 71.0 MPa ISO 527-2/5 |
Tensile Strain, Break 2.7 % ISO 527-2/5 |
Flexural Modulus(2 mm/min) 6200 MPa ISO 178 |
Flexural Stress, at Yield(2 mm/min) 122 MPa ISO 178 |
Flexural strain at break(2 mm/min) 4.5 % ISO 178 |
Notched Izod Impact Strength(23 °C) 4.0 kJ/m² ISO 180/1A |
Unnotched Izod Impact Strength(23 °C) 35 kJ/m² ISO 180/1U |
Thermal Nominal Value Test Method |
Heat Deflection Temperature, Unannealed |
0.45 MPa;64 mm;Span;80x10x4 mm 179 °C ISO 75-2/Bf |
1.8 MPa;64 mm;Span;80x10x4 mm 94.0 °C ISO 75-2/Af |
CLTE, Flow(23 - 60 °C) 6.4E-5 cm/cm/°C ISO 11359-2 |
CLTE, Transverse(23 - 60 °C) 7.7E-5 cm/cm/°C ISO 11359-2 |
Flame Rating(0.8 mm;E2P Measurement) V-2 UL 94 |
Processing |
Nominal Value |
Drying Temperature<Injection> |
80 °C |
Drying Time<Injection> |
4.0 hr |
Suggested Max Moisture<Injection> |
0.20 % |
Rear Temperature<Injection> |
245 - 255 °C |
Middle Temperature<injection> |
250 - 260 °C |
Front Temperature<Injection> |
250 - 260 °C |
Processing Temp, Melt<Injection> |
255 - 265 °C |
Mold Temperature<Injection> |
55 - 95 °C |