Product Description | |
MVR (330°C/2.16kg) 45 cm³/10 min; low viscosity; easy release; UV stabilized; 'softening temperature (VST/B 120) =157°C; injection molding - melt temperature 320 - 340°C | |
General | |
Form | Resin Pellets |
Outdoor Medium-Low Viscosity Enhanced Stiffness | |
Feature Excellent Processability High Clarity High Impact | |
Good Thermal | |
Physical Nominal Value Test Method | |
Density / Specific Gravity(23 °C) 1.18 g/cm³ ISO 1183 | |
Melt Mass-Flow Rate, MFR(2.16 kg;330 °C) 46 g/10min ISO 1133 | |
Melt Volume-Flow Rate, MVR(2.16 kg;330 °C) 45 cm³/10 min ISO 1133 | |
Water Absorption, Saturation(23 °C) 0.30 % ISO 62 | |
Water Absorption, Equilibrium(50% RH;23 °C) 0.12 % ISO 62 | |
Mechanical Nominal Value Test Method | |
Tensile Modulus(23 °C) 2400 MPa ISO 527-2/1 | |
Tensile Stress, Yield(23 °C) 68.0 MPa ISO 527-2/50 | |
Tensile Strain, Yield(23 °C) 6.2 % ISO 527-2/50 | |
Nominal Tensile Strain at Break(23 °C) > 50 % ISO 527-2/50 | |
C harpy Unnotched Impact Strength ISO 179 1eU | |
-30 °C No Break | |
23 °C No Break |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
149 °C 137 °C |
ISO 75-2/B ISO 75-2/A |
Vicat Softening Temperature | 157 °C | ISO 306/B120 |
CLTE, Flow(23 - 55 °C) | 6.5E-5 cm/cm/°C | ISO 11359-2 |
CLTE, Transverse(23 - 55 °C) | 6.5E-5 cm/cm/°C | ISO 11359-2 |
RTI Elec | 140 °C | UL 746 |
RTI Imp | 130 °C | UL 746 |
RTI Str | 140 °C | UL 746 |
Flame Rating 1.5 mm 3 mm |
HB HB |
UL 94 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+16 ohms | IEC 60093 |
Volume Resistivity(23 °C) | 1.0E+17 ohms ·cm | IEC 60093 |
Electric Strength(23 °C;1 mm) | 35 kV/mm | IEC 60243-1 |
Relative Permittivity 100 Hz;23 °C 23 °C;1.0e+6 Hz |
3.00 2.90 |
IEC 60250 |
Dissipation Factor 100 Hz;23 °C 23 °C;1.0e+6 Hz |
1.0E-3 9.0E-3 |
IEC 60250 |
Comparative Tracking Index, Solution A | 250 V | IEC 60112 |
Comparative Tracking Index, Solution B | 125 V | IEC 60112 |
Optical | Nominal Value | Test Method |
Refractive Index, Method A | 1.578 | ISO 489 |
Transmittance (1.0e+3 µm) | 89.0 % | ISO 13468-2 |
Chemical | Nominal Value | Test Method |
Electrolytical Corrosion(23 °C) | A1 | IEC 60426 |
Processing | Nominal Value |
Drying Temperature - Dry Air Dryer<Injection> | 130 °C |
Drying Time - Dry Air Dryer<Injection> | 2.0 - 4.0 hr |
Suggested Max Moisture<Injection> | < 0.020 % |
Suggested Shot Size<Injection> | 30 - 70 % |
Rear Temperature<Injection> | 310 - 320 °C |
Middle Temperature<injection> | 315 - 325 °C |
Front Temperature<Injection> | 315 - 330 °C |
Nozzle Temperature<Injection> | 310 - 335 °C |
Processing Temp, Melt<Injection> | 320 - 340 °C |
Mold Temperature<Injection> | 80 - 120 °C |
Back Pressure<Injection> | 10.0 - 20.0 MPa |
Vent Depth <Injection> | 0.025 - 0.050 mm |