Feature: | Oxidative Degradable |
---|---|
CAS No.: | 32131-17-2 |
Formula: | (C12h22n2o2)N |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Glass Fiber Reinforced Polyamide 6 Injection Molding Resin with Improved Thermal Conductivityhttps://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html
PA6 with 30%GF reinforced, used for the automotive industry, Electrical and Electronics and consumer applications
General |
||
Form Resin Pellets |
||
Filler 30 % Glass Fiber |
||
High Impact Easy Release Excellent Mechanical |
||
Feature High Mechanical Strength
|
||
Automotive Industry (interior And Body Parts) |
||
Physical Nominal Value Test Method |
||
Density / Specific Gravity 1.37 g/cm³ ISO 1183 |
||
Water Absorption(23 0 ºC) 6.7 % ISO 62 |
||
Melt Volume Rate, MVR 50 cm³/10 min ISO 1133 |
||
Mechanical Nominal Value Test Method |
||
Tensile Modulus 9500 MPa ISO 527 |
||
Flexural Modulus 8500 MPa ISO 178 |
||
Flexural Strength 270 MPa ISO 178 |
||
C harpy Impact Strength, Unnotched 95 kJ/m² ISO 179 |
||
C harpy Impact Strength, Notched(23 ºC) 10 kJ/m² ISO 179 |
||
Thermal Nominal Value Test Method |
||
Deflection Temperature Under Load, ISO ISO 75 |
||
1.8 MPa 210 °C |
||
0.45 MPa 220 °C |
||
CLTE, Transverse 0.25E-4 - 0.7E-4 /K ISO 11359 |
||
UL temperature rating HB UL 94 |
||
Melting Point(DSC) |
220 °C |
|
Processing |
Nominal Value |
|
Melt Temperature Range |
270 - 290 °C |
|
Mold temperature range |
80 - 100 °C |
Forever Co.,Ltd