Polyamine Nylon PPA Material is glass fiber reinforced PPA products
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | |
Sinowin New Material TG845 BK010 is glass fiber reinforced PPA products. | |
General | |
Form Resin Pellets | |
Filler 45 % Glass Fiber | |
Feature Smt(Reflow) Chemical Resistant Good Thermal | |
Uses Automotive Trumpet cover | |
Physical Nominal Value Test Method | |
Density, dry(23 °C) 1.53 g/cm³ ASTM D792 | |
Dry: Moulding shrinkage, parallel(3.2 mm) 0.3 % ASTM D955 | |
Dry: Moulding shrinkage, normal(3.2 mm) 0.7 % ASTM D955 | |
Water Absorption(50% RH;23 ºC) 0.6 % ASTM D570 | |
Mechanical Nominal Value Test Method | |
Dry: Tensile Strength(5 mm/min) 165 MPa ASTM D638 | |
Dry: Tensile Elongation, Break(5 mm/min) 1.0 % ASTM D 638 | |
Dry: Flexural Modulus(2 mm/min) 10000 MPa ASTM D790 | |
Dry: Flexural Strength(2 mm/min) 250 MPa ASTM D790 | |
Dry: Izod Notched Impact Strength(3.175;23 °C) 160 J/m ASTM D256 | |
Thermal Nominal Value Test Method | |
Dry: Melting Temperature(First Heat) 310 °C ASTM D789 | |
Dry: Temp. of deflection under load(1.82 MPa) 285 °C ASTM D648 | |
Flammability, UL94(1.6 mm) HB UL 94 | |
Electrical Nominal Value Test Method | |
Dry: Volume Resistivity 1.0E+12 ASTM D257 | |
Dielectric Constant(1.0e+9 Hz) 3.5 ASTM D150 | |
Dissipation Factor(1.0e+9 Hz) 0.012 ASTM D150 | |
CTI(Solution A) PLC 2 IEC 60112 | |
Processing | Nominal Value |
Drying Temperature | 110 - 130 °C |
Drying Time | 4 - 6 hrs |
Maximum Moisture Content | ≤ 0.2 % |
Front Barrel Temperature | 310 - 330 °C |
Middle Barrel Temperature | 290 - 320 °C |
Rear Barrel Temperature | 290 - 320 °C |
Nozzle Temperature | 310 - 330 °C |
Mold Temperature | 80 - 120 °C |
Injection Speed | |
Injection Pressure | |
Back Pressure | 0 - 5 MPa |