Hostaform® MT8U01 is an injection molding grade with a molecular weight for excellent moldability and optimum properties in demanding applications. Hostaform MT8U01 is a special grade developed for medical industry applications and complies with: CFR 21 (177.2470) of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 11559) and the Device Master File (MAF 1079) the corresponding EU and national registry regulatory requirements biocompatibility in tests corresponding to USP <88> Class VI/ISO 10993 low residual monomers no animal-derived constituents | ||||
General | ||||
Form | Resin Pellets | |||
Biocompatible | No Animal Derived | Dmf 11559 | ||
Feature | Components | Fda | ||
Maf | ||||
Uses | Medical | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.41 g/cm³ | ISO 1183 | ||
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) | 8.0 cm³/10 min | ISO 1133 | ||
Molding Shrinkage, Across Flow | 1.8 % | ISO 294-4 | ||
Molding Shrinkage, Flow | 2.0 % | ISO 294-4 | ||
Water Absorption, Saturation(23 °C) | 0.65 % | ISO 62 | ||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.20 % | ISO 62 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus | 2850 MPa | ISO 527-2/1A | ||
Tensile Stress, Yield | 64.0 MPa | ISO 527-2/1A/50 | ||
Tensile Strain, Yield | 9.0 % | ISO 527-2/1A/50 | ||
Nominal Tensile Strain at Break | 30 % | ISO 527-2/1A/50 | ||
Tensile creep modulus | ISO 899-1 | |||
1 hr | 2500 MPa | |||
1000 hr | 1300 MPa | |||
Flexural Modulus(23 °C) | 2700 MPa | ISO 178 | ||
Charpy Notched Impact Strength | ISO 179 1eA | |||
-30 °C | 6.0 kJ/m² | |||
23 °C | 6.5 kJ/m² | |||
Charpy Unnotched Impact Strength(-30 °C) | 220 kJ/m² | ISO 179 1eU | ||
Charpy Unnotched Impact Strength, Partial Break(23 °C) | 220 kJ/m² | ISO 179 1eU |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed(1.8 MPa) | 104 °C | ISO 75-2/A |
Vicat Softening Temperature | 150 °C | ISO 306/B50 |
Melting Point(10 °C/min) | 166 °C | ISO 11357-3 |
CLTE, Flow | 1.1E-4 cm/cm/°C | ISO 11359-2 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 100 - 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.15 % | |
Hopper Temperature<Injection> | 20 - 30 °C | |
Rear Temperature<Injection> | 170 - 180 °C | |
Middle Temperature<injection> | 180 - 190 °C | |
Front Temperature<Injection> | 190 - 200 °C | |
Nozzle Temperature<Injection> | 190 - 210 °C | |
Processing Temp, Melt<Injection> | 190 - 210 °C | |
Mold Temperature<Injection> | 80 - 120 °C | |
Feeding Zone Temperature<Injection> | 60 - 80 °C | |
Zone4 temperature<Injection> | 190 - 210 °C | |
Hot Runner Temperature<Injection> | 190 - 210 °C |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |