Resin Pellets Filler 35 % Glass Fiber FeatureHigh Mechanical Stren Polyamine Nylon PPA
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
General | ||||
Form Resin Pellets | ||||
Filler 35 % Glass Fiber | ||||
Feature |
High Mechanical Strength | Good Thermal High Strength |
Good Dimensional | |
And Rigidity | ||||
Uses Industria Automotive | ||||
Physical Nominal Value Test Method | ||||
Density / Specific Gravity 1.42 g/cm³ ISO 1183 | ||||
Molding Shrinkage, Flow 0.3 - 0.6 % ISO 294-4 | ||||
Molding Shrinkage, Across Flow 0.2 - 0.4 % ISO 294-4 | ||||
Mechanical Nominal Value Test Method | ||||
Tensile Strength(20 mm/min) 175 MPa ISO 527-2 | ||||
Elongation at Break(20 mm/min) 2.8 % ISO 527-2 | ||||
Flexural Strength(2 mm/min) 275 MPa ISO 178 | ||||
Flexural Modulus(2 mm/min) 9450 MPa ISO 178 | ||||
Notched Izod Impact Strength 10 kJ/m² ISO 180 | ||||
Thermal Nominal Value Test Method | ||||
Deflection Temperature ASTM D648 | ||||
0.45 MPa 280 °C | ||||
1.82 MPa 262 °C | ||||
Flammability(1.6 mm) HB UL94 | ||||
Processing Nominal Value | ||||
Drying Temperature 130 - 150 °C | ||||
Drying Time 2 - 4 | ||||
Mold Temperature 120 - 150 °C | ||||
Melt Temperature 290 - 330 °C |