Xht2146 Resin Is a High Flow High Heat Polycarbonate Copolymer

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC-XHT2146
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Natural Color
• Place of Origin: Guangdong, China
• Use: Radiator Front Cover.Automotive Parts
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Delivery Time: in 7 Days
• Applications: Appliance Handles, Spotlights, Electric Motors.
• Glass Fiber: 0%
• Gr: 0%
• Carbon Fiber: 0 %
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

XHT2146 resin is a high flow high heat polycarbonate copolymer

    

Product Description
XHT2146 resin is a high flow, high heat polycarbonate copolymer with improved release performance compared to  XHT2141 resin. It is available in a range of opaque and limited transparent colors.
General
Form                                        Resin Pellets
Feature                                     Good Thermal
Uses                                         Automotive
Physical                                                                                 Nominal Value                                       Test Method
Density / Specific Gravity 1.2                                                         ASTM D792 1.2 g/cm³                                              ISO 1183
Mold Shrinkage, Flow(3.2 mm)                                           0.6 - 0.9 %                                                Method
Melt Flow Rate[MFR](330 °C;2.16 kgf)                                46 g/10min                                            ASTM D1238
Water Absorption(23 °C;saturated)                                    0.3 %                                                      ISO 62-1
Moisture Absorption(50% RH;23 °C)                                  0.23 %                                                     ISO 62
Melt Volume Rate, MVR(2.16 kg;330 °C)                            43 cm³/10 min                                        ISO 1133
Mechanical                                                                            Nominal Value                                      Test Method
Izod Impact, Notched
23 °C                                                                                    115 J/m                                                   ASTM D256
-30 °C                                                                                  75 J/m                                                     ASTM D256
80*10*4;23 °C                                                                      11 kJ/m²                                                 ISO 180/1A
80*10*4;-30 °C                                                                    10 kJ/m²                                                 ISO 180/1A
Instrumented Dart Impact, Total Energy(23 °C)                 68 J                                                         ASTM D3763
Unnotched Izod Impact Strength                                                                                                      ISO 180/1U
unnotched;80*10*3;23 °C 0                                                NB kJ/m²
unnotched;80*10*3;-30 °C 0                                              NB kJ/m²
Notched Izod Impact Strength                                                                                                          ISO 180/1A
notched;80*10*3;23 °C 0                                                    10 kJ/m²
notched;80*10*3;-30 °C 0                                                  9 kJ/m²
C harpy Impact, V-Notched                                                                                                                 ISO 179 1eA
23 °C;Edgew;80*10*3;sp =62mm 0                                     12 kJ/m²
-30 °C;Edgew;80*10*3;sp =62mm 0                                   9 kJ/m²
23 °C;Edgew;80*10*4;sp =62 mm 0                                    20 kJ/m²
C harpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0	NB kJ/m² NB kJ/m²	ISO 179 1eU
Tensile Stress, Yield
50 mm/min;Type I	70 MPa	ASTM D638
50 mm/min	70 MPa	ISO 527
Tensile Stress, Break
50 mm/min;Type I	60 MPa	ASTM D638
50 mm/min	60 MPa	ISO 527
Tensile Strain, Yield
50 mm/min;Type I	6.5 %	ASTM D638
50 mm/min	6.5 %	ISO 527
Tensile Strain, Break
50 mm/min;Type I	90 %	ASTM D638
50 mm/min	90 %	ISO 527
Tensile Modulus
5 mm/min	2600 MPa	ASTM D638
1 mm/min	2600 MPa	ISO 527
Flexural Stress, Yield
1.3 mm/min;50 mm;span	110 MPa	ASTM D790
2 mm/min	100 MPa	ISO 178
Flexural Modulus
1.3 mm/min;50 mm;span	2550 MPa	ASTM D790
2 mm/min	2450 MPa	ISO 178
Thermal	Nominal Value	Test Method
Vicat Softening Temperature
Rate B/50	161 °C	ASTM D1525
Rate B/50	160 °C	ISO 306
Rate B/120	162 °C	ISO 306
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa	155 °C 145 °C	ASTM D648
CTE, Flow
-40 - 40 °C	6.0E-05 1/°C	ASTM E831
-40 - 40 °C	6.0E-05 1/°C	ISO 11359-2
CTE, XFlow
-40 - 40 °C	6.0E-05 1/°C	ASTM E831
-40 - 40 °C	6.0E-05 1/°C	ISO 11359-2
HDT/Bf(0.45)	155 °C	ISO 75/Bf
HDT/Af(1.8)	142 °C	ISO 75/Af
Metallized Haze Onset	155 °C	Method
Processing		Nominal Value
Drying Temperature<Injection>		125 °C
Drying Time<Injection>		4 - 6 hrs
Maximum Moisture Content<Injection>		0.02 %
Melt Temperature<Injection>		290 - 350 °C
Nozzle Temperature<Injection>		285 - 345 °C
Front, Zone 3 Temperature<Injection>		290 - 350 °C
Middle, Zone 2 Temperature<Injection>		280 - 340 °C
Rear, Zone 1 Temperature<Injection>		270 - 330 °C
Mold Temperature<Injection>		85 - 130 °C
Back Pressure<Injection>		0.3 - 0.7 MPa
Screw Speed <Injection>		40 - 90 rpm
Shot To Cylinder Size<Injection>		40 - 60 %
Vent Depth <Injection>		0.025 - 0.08 mm

  

Company Profile

Product Parameters

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry