| Customization: | Available |
|---|---|
| Feature: | Plastics |
| CAS No.: | 25766-59-0 |
|
Still deciding? Get samples of US$ 1/kg
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment methods: |
|
|---|---|
| Support payment in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| General | ||
| Form Resin Pellets | ||
| Filler 30 % Glass Fiber | ||
| Feature | High Impact Lds |
Enhanced Ductility Circuit Solution Good Surface Appearance |
| Usage | Automotive Electrical |
Consumer Laser Direct Structuring |
| Physical Nominal Value Test Method | ||
| Density / Specific Gravity 1.47 ASTM D792 | ||
| Melt Flow Rate[MFR] ASTM D1238 | ||
| 280 °C;2.16 kgf 10 g/10min | ||
| 280 °C;5 kgf 27 g/10min | ||
| 300 °C;1.2 kgf 16 g/10min | ||
| Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) 13 cm³/10 min ASTM D1238 | ||
| Mechanical | Nominal Value | Test Method |
| C harpy Impact, Unnotched(23 °C) | 50 kJ/m² | ISO 179/2C |
| Izod Impact, Unnotched | ||
| 23 °C | 700 J/m | ASTM D4812 |
| 80*10*4;23 °C | 40 kJ/m² | ISO 180/1U |
| Izod Impact, Notched | ||
| 23 °C | 150 J/m | ASTM D256 |
| 80*10*4;23 °C | 14 kJ/m² | ISO 180/1A |
| C harpy Impact, Notched(23 °C) | 14 kJ/m² | ISO 179/2C |
| Tensile Stress, Break | ||
| 5 mm/min;Type I | 120 MPa | ASTM D638 |
| 50 mm/min | 120 MPa | ISO 527 |
| Tensile Strain, Break | ||
| 5 mm/min;Type I | 2.4 % | ASTM D638 |
| 50 mm/min | 2.4 % | ISO 527 |
| Tensile Modulus | ||
| 5 mm/min | 8760 MPa | ASTM D638 |
| 1 mm/min | 8840 MPa | ISO 527 |
| Flexural Stress | ||
| 170 MPa | ASTM D790 | |
| 180 MPa | ISO 178 | |
| Flexural Modulus | ||
| 8020 MPa | ASTM D790 | |
| 8450 MPa | ISO 178 |
| Thermal | Nominal Value | Test Method |
| Heat Deflection Temperature[HDT] 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
126 °C 122 °C |
ASTM D648 |
| CTE, Flow -40 - 40 °C -40 - 40 °C |
2.1e-05 1/°C 2.1e-05 1/°C |
ASTM E831 ISO 11359-2 |
| CTE, XFlow -40 - 40 °C -40 - 40 °C |
6.9e-05 1/°C 7.1e-05 1/°C |
ASTM E831 ISO 11359-2 |
| HDT/Bf(0.45) | 127 °C | ISO 75/Bf |
| HDT/Af(1.8) | 124 °C | ISO 75/Af |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 110 °C | |
| Drying Time<Injection> | 3 - 4 hrs | |
| Melt Temperature<Injection> | 270 - 295 °C | |
| Nozzle Temperature<Injection> | 270 - 295 °C | |
| Front, Zone 3 Temperature<Injection> | 270 - 295 °C | |
| Middle, Zone 2 Temperature<Injection> | 270 - 295 °C | |
| Rear, Zone 1 Temperature<Injection> | 270 - 295 °C | |
| Mold Temperature<Injection> | 100 - 120 °C |