CAS No.: | 9002-98-6 |
---|---|
Formula: | C39h30n2o6 |
EINECS: | 205-793-9 |
Samples: |
BAG
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | ||||||||||||
ULTEM HU2310 resin is an improved flow, 30% glass fiber reinforced polyetherimide resin. The intended use for this material is in medical devices and pharmaceutical applications. The material offers biocompatibility (ISO 10993 or USP Class VI) and Healthcare management of change applies. The material may offer Steam-, Hydrogen Peroxide-, Gamma-, EtO-, UV-C- and E-beam resistance for repeated sterilization cycles. It may offer global food compliance (FDA, CN, EC). The material is RoHS compliant and is intrinsically flame retardant without the use of FR modifiers. It offers UL94 V0 and 5VA ratings. The material can also offer excellent dimension stability, strength, stiffness and creep resistance up to high temperature due to its high glass transition temperature of 217°C. The material is opaque and can be custom colored. |
||||||||||||
General | ||||||||||||
Form | Resin Pellets | |||||||||||
Filler | 30 % Glass Fiber | |||||||||||
Feature |
Biocompatible Steam Sterilization | Easy Release | ||||||||||
Fda Good Dimensional | Good Thermal | |||||||||||
Good Hardness Hydrolysis Resistance | Amorphous | |||||||||||
Good Mechanicals Low Smoke | Low Creep Sensitivity | |||||||||||
Good Metal Adhesion Gamma Sterilizable | Eto And E-Beam Sterilizable |
|||||||||||
UL Yellow Card | E121562-221099 | |||||||||||
Uses | Consumer | Healthcare | ||||||||||
Physical | Nominal Value | Test Method | ||||||||||
Density / Specific Gravity | ||||||||||||
1.51 g/cm³ | ISO 1183 | |||||||||||
1.51 | ASTM D792 | |||||||||||
Moisture Absorption 23 °C;50% RH/24hrs 23 °C;50% RH/Equilibrium |
0.1 % 0.6 % |
ISO 62-4 | ||||||||||
Water Absorption | ||||||||||||
24 hrs;23 °C | 0.16 % | ISO 62-1 | ||||||||||
23 °C;saturated | 0.9 % | ISO 62-1 | ||||||||||
24 hrs;23 °C | 0.16 % | ASTM D570 | ||||||||||
23°C/Saturated | 0.9 % | ASTM D570 | ||||||||||
Melt Volume Rate, MVR(5 kg;MVR at 360 °C) | 8 cm³/10 min | ISO 1133 | ||||||||||
Melt Flow Rate[MFR](337 °C;6.6 kgf) | 7.6 g/10min | ASTM D1238 | ||||||||||
Mold Shrinkage, Flow(3.2 mm) | 0.2 - 0.4 % | Method | ||||||||||
Hardness, Rockwell M | ||||||||||||
110 | ISO 2039-2 | |||||||||||
114 | ASTM D785 | |||||||||||
Mechanical | Nominal Value | Test Method | ||||||||||
Izod Impact, Notched | ||||||||||||
80*10*4;23 °C | 10 kJ/m² | ISO 180/1A | ||||||||||
80*10*4;-30 °C | 10 kJ/m² | ISO 180/1A | ||||||||||
23 °C | 90 J/m | ASTM D256 | ||||||||||
-30 °C | 80 J/m | ASTM D256 | ||||||||||
Izod Impact, Unnotched | ||||||||||||
80*10*4;23 °C | 40 kJ/m² | ISO 180/1U | ||||||||||
80*10*4;-30 °C | 40 kJ/m² | ISO 180/1U | ||||||||||
23 °C | 600 J/m | ASTM D4812 | ||||||||||
-30 °C | 600 J/m | ASTM D4812 | ||||||||||
C harpy Impact, V-Notched 23 °C;Edgew;80*10*4;sp =62 mm 0 -30 °C;Edgew;80*10*4;sp =62 mm 0 |
10 kJ/m² 10 kJ/m² |
ISO 179 1eA | ||||||||||
C harpy Impact, Unnotched 23 °C;Edgew;80*10*4;sp =62 mm 0 -30 °C;Edgew;80*10*4;sp =62 mm 0 |
40 kJ/m² 40 kJ/m² |
ISO 179 1eU | ||||||||||
Izod Impact, Reverse Notched(3.2 mm) | 470 J/m | ASTM D256 | ||||||||||
Tensile Stress, Break | ||||||||||||
5 mm/min | 175 MPa | ISO 527 | ||||||||||
5 mm/min;Type I | 175 MPa | ASTM D638 | ||||||||||
Tensile Strain, Break | ||||||||||||
5 mm/min | 2.4 % | ISO 527 | ||||||||||
5 mm/min;Type I | 2.5 % | ASTM D638 | ||||||||||
Tensile Modulus | ||||||||||||
1 mm/min | 1.0E+04 MPa | ISO 527 | ||||||||||
5 mm/min | 1.0E+04 MPa | ASTM D638 | ||||||||||
Flexural Stress, break | ||||||||||||
2 mm/min | 240 MPa | ISO 178 | ||||||||||
2.6 mm/min;100 mm;Span | 230 MPa | ASTM D790 | ||||||||||
1.3 mm/min;50 mm;span | 250 MPa | ASTM D790 | ||||||||||
Flexural Modulus | ||||||||||||
2 mm/min | 9600 MPa | ISO 178 | ||||||||||
2.6 mm/min;100 mm;Span | 9400 MPa | ASTM D790 | ||||||||||
1.3 mm/min;50 mm;span | 9700 MPa | ASTM D790 | ||||||||||
Ball Indentation Hardness(H358/30) | 165 MPa | ISO 2039-1 | ||||||||||
Taber Abrasion(CS-17;1 kg;1000cy) | 20 mg | Method | ||||||||||
Thermal | Nominal Value | Test Method | ||||||||||
UL Recognized ≥ 1.2 mm ≥ 0.25 mm |
5VA V-0 |
UL 94 | ||||||||||
Glow Wire Ignition Temperature [GWIT](2 mm) | 900 °C | IEC 60695-2-13 | ||||||||||
Glow Wire Flammability Index(2 mm) | 960 °C | IEC 60695-2-12 | ||||||||||
Oxygen Index | 48 % | ISO 4589 | ||||||||||
HDT/Bf(0.45) | 215 °C | ISO 75/Bf | ||||||||||
HDT/Af(1.8) | 210 °C | ISO 75/Af | ||||||||||
Vicat Softening Temperature Rate A/50 Rate B/120 Rate B/50 |
225 °C 220 °C 213 °C |
ISO 306 | ||||||||||
CTE, Flow -20°C to 150°C -20°C to 150°C |
1.7E-05 1/°C 1.9E-05 1/°C |
ISO 11359-2 ASTM E831 |
||||||||||
CTE, XFlow -20°C to 150°C -20°C to 150°C |
4.9E-05 1/°C 4.1E-05 1/°C |
ISO 11359-2 ASTM E831 |
||||||||||
Thermal Conductivity | 0.31 W/m-K | ISO 8302 | ||||||||||
Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 | ||||||||||
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 0.45 MPa;6.4 mm 3.2 mm;1.82 MPa 1.82 MPa;6.4 mm |
215 °C 212 °C 211 °C 210 °C |
ASTM D648 | ||||||||||
Relative Temp Index, Elec | 180 °C | UL 746B | ||||||||||
Relative Temp Index, Mechanical with Impact | 170 °C | UL 746B | ||||||||||
Relative Temp Index, Mechanical without Impact | 180 °C | UL 746B | ||||||||||
Electrical | Nominal Value | Test Method | ||||||||||
Volume Resistivity | 1.0e+15 ohms ·cm 3.0E+16 ohms ·cm |
IEC 60093 ASTM D257 |
||||||||||
Surface Resistivity, ROA | > 1.E+15 Ohms | IEC 60093 | ||||||||||
Dielectric Strength, in Oil | ||||||||||||
0.8 mm | 35 kV/mm | IEC 60243-1 | ||||||||||
1.6 mm | 26 kV/mm | IEC 60243-1 | ||||||||||
3.2 mm | 15 kV/mm | IEC 60243-1 | ||||||||||
1.6 mm | 30.3 kV/mm | ASTM D149 | ||||||||||
Relative Permittivity | ||||||||||||
50/60 Hz | 3.3 | IEC 60250 | ||||||||||
1.0e+6 Hz | 3.4 | IEC 60250 | ||||||||||
1.0e+3 Hz | 3.7 | ASTM D150 | ||||||||||
Dissipation Factor | ||||||||||||
50/60 Hz | 1.6E-03 | IEC 60250 | ||||||||||
1.0e+6 Hz | 2.5E-03 | IEC 60250 | ||||||||||
1.1e+9 Hz | 2.9E-03 | |||||||||||
5.0e+9 Hz | 3.6E-03 | |||||||||||
1.0e+10 Hz | 4.6E-03 | |||||||||||
1.0e+3 Hz | 1.5E-03 | ASTM D150 | ||||||||||
Dielectric Constant | ||||||||||||
1.1e+9 Hz | 3.51 | |||||||||||
5.0e+9 Hz | 3.59 | |||||||||||
1.0e+10 Hz | 3.6 | |||||||||||
Comparative Tracking Index | 150 V | IEC 60112 | ||||||||||
Comparative tracking index M | 100 V | IEC 60112 | ||||||||||
Dielectric Strength, in Air(1.6 mm) | 24.8 kV/mm | ASTM D149 | ||||||||||
Comparative Tracking Index, CTI | PLC4 | UL 746A | ||||||||||
Hot-wire Ignition, HWI ≥ 3 mm ≥ 1.5 mm |
PLC 1 PLC 3 |
UL 746A | ||||||||||
High Amp Arc Ignition, HAI ≥ 1.5 mm ≥ 3 mm |
PLC 3 PLC4 |
UL 746A | ||||||||||
High Voltage Arc Tracking Rate, HVTR | PLC 3 | UL 746A | ||||||||||
Arc Resistance, Tungsten Electrode | PLC 6 | ASTM D495 | ||||||||||
Processing | Nominal Value | |||||||||||
Drying Temperature<Injection> | 150 °C | |||||||||||
Drying Time<Injection> | 4 - 6 hrs | |||||||||||
Drying Time, Cumulative<Injection> | 24 hrs | |||||||||||
Maximum Moisture Content<Injection> | 0.02 % | |||||||||||
Melt Temperature<Injection> | 350 - 410 °C | |||||||||||
Nozzle Temperature<Injection> | 345 - 410 °C | |||||||||||
Front, Zone 3 Temperature<Injection> | 345 - 420 °C | |||||||||||
Middle, Zone 2 Temperature<Injection> | 340 - 410 °C | |||||||||||
Rear, Zone 1 Temperature<Injection> | 330 - 400 °C | |||||||||||
Hopper Temperature<Injection> | 80 - 120 °C | |||||||||||
Mold Temperature<Injection> | 135 - 180 °C | |||||||||||
Shot To Cylinder Size<Injection> | 40 - 60 % | |||||||||||
Vent Depth <Injection> | 0.025 - 0.076 mm | |||||||||||
Screw Speed <Injection> | 40 - 70 rpm | |||||||||||
Screw Speed, C ircumferential Speed <Injection> | 0.15 - 0.25 m/s | |||||||||||
Back Pressure<Injection> | 0.3 - 1.5 MPa |
Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.
Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.
With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry
Suppliers with verified business licenses