Feature: | Plastics |
---|---|
CAS No.: | 63440-93-7 |
Formula: | C24h24o8 |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
General |
||||
Form |
Resin Pellets |
|||
Feature |
Chemical Resistant
Non-Chlorinated |
Hydrolysis Resistance
Thin Wall |
Non-Brominated & Non- Chlorinated Flame
Retardant |
|
Usage Healthcare |
Electrical |
Building and Construction |
||
Physical |
Nominal Value |
Test Method |
||
Density / Specific Gravity |
1.19 1.19 g/cm³ |
ASTM D792 ISO 1183 |
||
Melt Flow Rate[MFR](260 °C;2.16 kgf) |
22.5 g/10min |
ASTM D1238 |
||
Water Absorption(23 °C;saturated) |
0.2 % |
ISO 62-1 |
||
Moisture Absorption(50% RH;23 °C) |
0.1 % |
ISO 62 |
||
Melt Volume Rate, MVR(2.16 kg;MVR at 260 °C) |
21 cm³/10 min |
ISO 1133 |
Mechanical |
Nominal Value |
Test Method |
Izod Impact, Notched 23 °C -30 °C |
600 J/m 120 J/m |
ASTM D256 |
Instrumented Dart Impact, Total Energy(23 °C) |
63 J |
ASTM D3763 |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
15 kJ/m² 10 kJ/m² |
ISO 180/1A |
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
15 kJ/m² 10 kJ/m² |
ISO 179 1eA |
Tensile Stress, Yield |
||
50 mm/min;Type I |
64 MPa |
ASTM D638 |
50 mm/min |
61 MPa |
ISO 527 |
Tensile Stress, Break |
||
50 mm/min;Type I |
54 MPa |
ASTM D638 |
50 mm/min |
51 MPa |
ISO 527 |
Tensile Strain, Yield |
||
50 mm/min;Type I |
4 % |
ASTM D638 |
50 mm/min |
4 % |
ISO 527 |
Tensile Strain, Break |
||
50 mm/min;Type I |
90 % |
ASTM D638 |
50 mm/min |
90 % |
ISO 527 |
Tensile Modulus |
||
50 mm/min |
2900 MPa |
ASTM D638 |
1 mm/min |
2700 MPa |
ISO 527 |
Flexural Stress, Yield |
||
1.3 mm/min;50 mm;span |
100 MPa |
ASTM D790 |
2 mm/min |
100 MPa |
ISO 178 |
Flexural Modulus |
||
1.3 mm/min;50 mm;span |
2700 MPa |
ASTM D790 |
2 mm/min |
2500 MPa |
ISO 178 |
Thermal |
Nominal Value |
Test Method |
UL Recognized ≥ 3 mm ≥ 2 mm ≥ 1.2 mm |
5VA 5VB V-0 |
UL 94 |
Vicat Softening Temperature |
||
Rate B/50 |
102 °C |
ASTM D1525 |
Rate B/50 |
102 °C |
ISO 306 |
Rate B/120 |
102 °C |
ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa 0.45 MPa;6.4 mm 1.82 MPa;6.4 mm |
94 °C 84 °C 98 °C 90 °C |
ASTM D648 |
CTE, Flow |
||
-40 - 40 °C |
7.5e-05 1/°C |
ASTM E831 |
-40 - 40 °C |
7.5e-05 1/°C |
ISO 11359-2 |
CTE, XFlow |
||
-40 - 40 °C |
7.5e-05 1/°C |
ASTM E831 |
-40 - 40 °C |
7.5e-05 1/°C |
ISO 11359-2 |
Thermal Conductivity |
0.2 W/m-K |
ISO 8302 |
Ball Pressure Test(75°C +/- 2°C) |
Pass |
IEC 60695-10-2 |
HDT/Af(1.8) |
84 °C |
ISO 75/Af |
Relative Temp Index, Elec |
90 °C |
UL 746B |
Relative Temp Index, Mechanical with Impact |
90 °C |
UL 746B |
Relative Temp Index, Mechanical without Impact |
90 °C |
UL 746B |
Processing |
Nominal Value |
Drying Temperature<Injection> |
80 - 90 °C |
Drying Time<Injection> |
3 - 4 hrs |
Drying Time, Cumulative<Injection> |
8 hrs |
Maximum Moisture Content<Injection> |
0.04 % |
Melt Temperature<Injection> |
245 - 275 °C |
Nozzle Temperature<Injection> |
245 - 275 °C |
Front, Zone 3 Temperature<Injection> |
245 - 275 °C |
Middle, Zone 2 Temperature<Injection> |
220 - 265 °C |
Rear, Zone 1 Temperature<Injection> |
220 - 255 °C |
Mold Temperature<Injection> |
60 - 80 °C |
Back Pressure<Injection> |
0.3 - 0.7 MPa |
Screw Speed <Injection> |
40 - 70 rpm |
Shot To Cylinder Size<Injection> |
30 - 80 % |
Vent Depth <Injection> |
0.038 - 0.076 mm |