Product Description | ||||||
HPH4504H resin is based on high heat Polycarbonate (PC) siloxane copolymer with enhanced autoclavability for medical devices and pharmaceutical applications. Added features of this grade include: Biocompatible (ISO10993 of USP Class VI). EtO, Steam, Gamma and e-Beam Sterilizable. |
||||||
General | ||||||
Form | Resin Pellets | |||||
Feature |
Biocompatible | Gamma Sterilizable | Eto Sterilization | |||
X-Ray Sterilizable | ||||||
UL Yellow Card | E121562-101338226 | |||||
Uses Pharmaceuticals Medical Device Medical | ||||||
Physical | Nominal Value | Test Method | ||||
Density / Specific Gravity | 1.19 g/cm³ 1.20 g/cm³ |
ASTM D792 ISO 1183 |
||||
Specific Volume | 0.830 cm³/g | ASTM D792 | ||||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 3.0 g/10min | ASTM D1238 | ||||
Melt Volume-Flow Rate, MVR | ISO 1133 | |||||
300 °C;1.2 kg | 3.0 cm³/10 min | |||||
2.16 kg;330 °C | 12 cm³/10 min | |||||
Molding Shrinkage, Flow(3.2 mm) | 0.70 - 0.80 % | Internal Method | ||||
Water Absorption(24 hr;23 °C) | 0.16 % | ASTM D570 | ||||
Water Absorption, Saturation(23 °C) | 0.16 % | ISO 62 | ||||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.35 % | ISO 62 | ||||
Rockwell Hardness, M-Scale | 85 | ASTM D785 | ||||
Rockwell Hardness, R-Scale | 122 | ASTM D785 | ||||
Mechanical | Nominal Value | Test Method | ||||
Tensile Modulus | ||||||
5 mm/min | 2090 MPa 2260 MPa |
ASTM D638 ISO 527-1/1 |
||||
Tensile Strength, Yield | ||||||
50 mm/min;Type I | 65.0 MPa 65.0 MPa |
ASTM D638 ISO 527-2/5;ISO 527-2/50 |
||||
Tensile Strength, Break | ||||||
50 mm/min;Type I | 71.0 MPa 65.0 MPa |
ASTM D638 ISO 527-2/50 |
||||
Tensile Elongation, Yield | ||||||
50 mm/min;Type I | 7.0 % 7.0 % |
ASTM D638 ISO 527-2/50 |
||||
Tensile Elongation, Break | ||||||
50 mm/min;Type I | 120 % > 50 % |
ASTM D638 ISO 527-2/50 |
||||
Flexural Modulus | ||||||
1.3 mm/min;50 mm;Span | 2020 MPa | ASTM D790 | ||||
2 mm/min | 2120 MPa | ISO 178 | ||||
Flexural Strength | ||||||
1.3 mm/min;50 mm;Span | 95.0 MPa | ASTM D790 | ||||
2 mm/min | 66.0 MPa | ISO 178 | ||||
C harpy Notched Impact Strength(23 °C;80*10*4;sp =62mm 0) |
15 kJ/m² | ISO 179/1eA | ||||
Notched Izod Impact | ||||||
-30 °C | 140 J/m | ASTM D256 | ||||
23 °C | 640 J/m | ASTM D256 | ||||
80*10*4 mm;-30 °C | 11 kJ/m² | ISO 180/1A | ||||
80*10*4 mm;23 °C | 13 kJ/m² | ISO 180/1A | ||||
Unnotched Izod Impact(23 °C) | 3200 J/m | ASTM D4812 | ||||
Instrumented Dart Impact, Total Energy(23 °C) | 73.0 J | ASTM D3763 | ||||
Gardner Impact(23 °C) | 149 J | ASTM D3029 | ||||
Tensile Impact Strength(Type S) | 577 kJ/m² | ASTM D1822 | ||||
Thermal | Nominal Value | Test Method | ||||
Deflection Temperature Under Load, Unannealed | ||||||
1.8 MPa;3.2 mm | 143 °C | ASTM D648 | ||||
80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 132 °C | ISO 75-2/Af | ||||
Vicat Softening Temperature | ||||||
50 °C/h;50 N;Rate A;Loading 2 | 160 °C 155 °C 154 °C |
ASTM D1525 ISO 306/B120 ISO 306/B50 | ||||
CLTE, Flow | ||||||
-40 - 40 °C | 6.0E-5 cm/cm/°C | ASTM E831;ISO 11359-2 | ||||
-40 - 95 °C | 9.2E-5 cm/cm/°C | ASTM E831 | ||||
CLTE, Transverse(-40 - 40 °C) | 6.0E-5 cm/cm/°C | ASTM E831;ISO 11359-2 | ||||
Specific Heat | 1260 J/kg/°C | ASTM C351 | ||||
Thermal Conductivity | 0.21 W/m-K | ASTM C177 | ||||
RTI Elec | 125 °C | UL 746B | ||||
RTI Imp | 125 °C | UL 746B | ||||
RTI Str | 125 °C | UL 746B | ||||
Flame Rating(> 1.5 mm) | HB | UL 94 | ||||
Electrical | Nominal Value | Test Method | ||||
Volume Resistivity | > 2.6E+17 ohms ·cm | ASTM D257 | ||||
Dielectric Strength, in Air(3.2 mm) | 20 kV/mm | ASTM D149 | ||||
Dielectric Constant 60 Hz 5.0e+4 Hz 1.0e+6 Hz |
3.15 3.15 3.00 |
ASTM D150 | ||||
Dissipation Factor 50 Hz 60 Hz 100 Hz |
1.2E-3 1.2E-3 0.024 |
ASTM D150 | ||||
Comparative Tracking Index, CTI | PLC 3 | UL 746A | ||||
High Amp Arc Ignition, HAI, Surface | PLC4 | UL 746A | ||||
High Voltage Arc Resistance to Ignition, HVAR | PLC 3 | UL 746A | ||||
Hot-wire Ignition, HWI | PLC 2 | UL 746A | ||||
Optical | Nominal Value | Test Method | ||||
Refractive Index | 1.600 | ASTM D542 | ||||
Transmittance (2.5e+3 µm) | 85.0 % | ASTM D1003 | ||||
Haze(2.5e+3 µm) | 1.00 % | ASTM D1003 | ||||
Processing | Nominal Value | |||||
Drying Temperature<Injection> | 120 °C | |||||
Drying Time<Injection> | 3.0 - 4.0 hr | |||||
Suggested Max Moisture<Injection> | 0.020 % | |||||
Suggested Shot Size<Injection> | 40 - 60 % | |||||
Rear Temperature<Injection> | 315 - 340 °C | |||||
Middle Temperature<injection> | 325 - 350 °C | |||||
Front Temperature<Injection> | 340 - 360 °C | |||||
Nozzle Temperature<Injection> | 330 - 355 °C | |||||
Processing Temp, Melt<Injection> | 340 - 360 °C | |||||
Mold Temperature<Injection> | 80 - 115 °C | |||||
Back Pressure<Injection> | 0.300 - 0.700 MPa | |||||
Screw Speed <Injection> | 40 - 70 rpm | |||||
Vent Depth <Injection> | 0.025 - 0.076 mm | |||||
Drying Time, Cumulative<Injection> | 48 hr |