Product Description |
CCP PBT PBT-4115 Application: Connectors, cooling fans, sockets, coil shafts, engine parts, switches, television parts, rectifiers Characteristic: Containing 15% glass fiber, high strength, flammability grade up to 1/32inch, UL94-V0, easy to form |
General |
Form Resin Pellets |
Filler 15 % Glass Fiber |
Feature High Strength Excellent Processability |
Uses |
Automotive Industry (interior And Body Parts) |
Connector Switches Electron & electric parts Socket |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.47 - 1.56 g/cm³ ASTM D792 |
Moisture Absorption(24 h) 0.03 % ASTM D570 |
Molding Shrinkage, Flow 0.3 - 0.6 % ASTM D955 |
Molding Shrinkage, Across Flow 1.2 - 1.8 % ASTM D955 |
Hardness, Rockwell, M-scale 93 ASTM D785 |
Mechanical Nominal Value Test Method |
Tensile Strength 88 - 108 MPa ASTM D638 |
Tensile Elongation 2.5 - 4.5 % ASTM D638 |
Flexural Strength 118 - 167 MPa ASTM D790 |
Flexural Elongation ≥ 4413 MPa ASTM D790 |
Izod impact strength, Notched(6.35 mm;bar 0) 39 - 69 J/m ASTM D256 |
Thermal Nominal Value Test Method |
Melting Point 225 °C DSC |
Heat Deflection Temperature ASTM D648 |
1.82 MPa 205 °C |
0.45 MPa 220 °C |
CLTE, Flow 5.5E-5 cm/cm/°C ASTM D696 |
Flammability(0.8 mm) V-0 UL 94 |
Electrical |
Nominal Value |
Test Method |
Dielectric Constant(60 Hz) |
3.3 |
ASTM D150 |
Dissipation Factor(60 Hz) |
0.001 |
ASTM D150 |
Volume Resistivity |
> 1.0E+15 ohms ·cm |
ASTM D257 |
Surface Resistance |
> 1.0E+13 ohms |
ASTM D257 |
Dielectric Strength(2 mm) |
> 20 KV/mm |
ASTM D149 |
Arc Resistance |
90 sec |
ASTM D495 |