Audited Supplier 45% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| AFA-6145 V0 Z is a 45% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both infrared and vapor phase soldering operations typically used by the electronics industry. Amodel® AFA-6145 V0 Z offers high flow and short molding cycles, thereby enhancing molding productivity and lowering costs. Black: AFA-6145 V0 Z BK 324 Natural: AFA-6145 V0 Z NT |
|||||||
| General | |||||||
| Form | Resin Pellets | ||||||
| Filler | 45 % Glass Fiber | ||||||
Feature |
Smt(Reflow) Chemical Resistant | Good Dimensional | |||||
| Good Electrical Properties | |||||||
| UL Yellow Card E95746-253235 | |||||||
| Automotive Electronics | Automotive Under The H d | Industrial Applications | |||||
Uses Automotive H i |
Cell Phone Cases | Industrial Parts Connector |
|||||
| ous ng | |||||||
| Physical | Nominal Value | Test Method | |||||
| Density / Specific Gravity | 1.80 g/cm³ | ISO 1183/A | |||||
| Molding Shrinkage, Flow | 0.20 % | ASTM D955 | |||||
| Molding Shrinkage, Across Flow | 0.40 % | ASTM D955 | |||||
| Mechanical | Nominal Value | Test Method | |||||
| Tensile Strength, Break | 193 MPa | ASTM D638 | |||||
| Tensile Elongation, Break | 1.5 % | ASTM D638 | |||||
| Flexural Modulus | 15500 MPa | ASTM D790 | |||||
| Flexural Strength | 276 MPa | ASTM D790 | |||||
| Notched Izod Impact | 110 J/m | ASTM D256 | |||||
| Thermal | Nominal Value | Test Method | |||||
| Deflection Temperature Under Load, Unannealed(1.8 MPa) | 277 °C | ASTM D648 | |||||
| Peak Melting Temperature | 310 °C | ASTM D3418 | |||||
| Flame Rating(0.79 mm) | V-0 | UL 94 | |||||
| Electrical | Nominal Value | Test Method | |||||
| Surface Resistivity | 1.0E+13 ohms | ASTM D257 | |||||
| Volume Resistivity | 1.0e+15 ohms ·cm | ASTM D257 | |||||
| Dielectric Strength(1.59 mm) | 23 kV/mm | ASTM D149 | |||||
| Dielectric Constant(1.0e+6 Hz) | 4.10 | ASTM D150 | |||||
| Dissipation Factor(1.0e+6 Hz) | 0.011 | ASTM D150 | |||||
| Comparative Tracking Index, CTI | PLC 1 | UL 746 | |||||
| High Amp Arc Ignition, HAI 0.75 mm 1.5 mm 3 mm |
PLC 1 PLC 1 PLC 1 |
UL 746 | |||||
| Hot-wire Ignition, HWI 0.75 mm 1.5 mm 3 mm |
PLC 0 PLC 0 PLC 0 |
UL 746 | |||||
| Processing | Nominal Value | ||||||
| Drying Temperature<Injection> | 120 °C | ||||||
| Drying Time<Injection> | 4.0 hr | ||||||
| Suggested Max Moisture<Injection> | 0.030 - 0.060 % | ||||||
| Rear Temperature<Injection> | 316 - 324 °C | ||||||
| Front Temperature<Injection> | 327 - 332 °C | ||||||
| Processing Temp, Melt<Injection> | 321 - 338 °C | ||||||
| Mold Temperature<Injection> | 66 - 93 °C | ||||||
| Injection Rate<Injection> | Fast 3 - 4 in/sec |
||||||