Feature: | Plastics |
---|---|
CAS No.: | 9003-56-9 |
Formula: | C45h51n3X2 |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | |||
General purpose ABS. Excellent flow/impact. | |||
General | |||
Form | Resin Pellets | ||
Uses | Appliances | Industrial Applications | |
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.04 g/cm³ | ASTM D792 | |
Melt Mass-Flow Rate, MFR(230 °C;3.8 kg) | 5.6 g/10min | ASTM D1238 | |
Melt Volume-Flow Rate, MVR(220 °C;10 kg) | 18 cm³/10 min | ISO 1133 | |
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.80 % | Internal Method | |
Melt Viscosity(240 °C;1.0e+3 sec^-1) | 225 Pa · s | ASTM D3835 | |
Mechanical | Nominal Value | Test Method | |
Tensile Modulus(5 mm/min) | 2130 MPa | ASTM D638 | |
Tensile Strength, Yield(5 mm/min;Type I) | 40.0 MPa | ASTM D638 | |
Tensile Strength, Break(5 mm/min;Type I) | 31.0 MPa | ASTM D638 | |
Tensile Elongation, Yield(5 mm/min;Type I) | 2.0 % | ASTM D638 | |
Tensile Elongation, Break(5 mm/min;Type I) | 20 % | ASTM D638 | |
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2200 MPa | ASTM D790 | |
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 68.0 MPa | ASTM D790 | |
Notched Izod Impact(23 °C) | 290 J/m | ASTM D256 | |
Instrumented Dart Impact, Total Energy(23 °C) | 30.0 J | ASTM D3763 | |
Thermal | Nominal Value | Test Method | |
Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm |
96.0 °C 82.0 °C |
ASTM D648 | |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 98.0 °C | ASTM D1525 | |
CLTE, Flow(-40 - 40 °C) | 8.8E-5 cm/cm/°C | ASTM E831 | |
CLTE, Transverse(-40 - 40 °C) | 8.8E-5 cm/cm/°C | ASTM E831 | |
RTI Elec | 60.0 °C | UL 746 | |
RTI Imp | 60.0 °C | UL 746 | |
RTI Str | 60.0 °C | UL 746 | |
Flame Rating(1.5 mm) | HB | UL 94 |
Electrical | Nominal Value | Test Method |
Arc Resistance, Tungsten Electrode | PLC 6 | ASTM D495 |
Comparative Tracking Index[CTI] | PLC 0 | UL 746 |
High Amp Arc Ignition, HAI, Surface | PLC 0 | UL 746 |
High Voltage Arc Tracking Rate, HVTR | PLC 3 | UL 746 |
Hot-wire Ignition, HWI | PLC 3 | UL 746 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 95 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.10 % | |
Suggested Shot Size<Injection> | 50 - 70 % | |
Rear Temperature<Injection> | 190 - 210 °C | |
Middle Temperature<injection> | 205 - 225 °C | |
Front Temperature<Injection> | 215 - 240 °C | |
Nozzle Temperature<Injection> | 220 - 260 °C | |
Processing Temp, Melt<Injection> | 220 - 260 °C | |
Mold Temperature<Injection> | 50 - 70 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed<Injection> | 30 - 60 rpm | |
Vent Depth<Injection> | 0.038 - 0.051 mm | |
Drying Time, Cumulative<Injection> | 8 hrs |