Feature: | Oxidative Degradable |
---|---|
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | ||||
LEXAN LUX9616G is an injection moldable polycarbonate (PC) with an MVR (300°C/1.2kg) 7. It contains non- brominated, non-chlorinated flame retardant systems with UL-94 V[email protected]mm rating. This UV stabilized grade has a diffusion effect and thin wall FR performance providing good color stability under heat exposure. | ||||
General | ||||
Form | Resin Pellets | |||
Feature | Non-Brominated Non-Chlorinated Outdoor | |||
UL Yellow Card E207780-101344669 | ||||
Appliances Electronic Displays |
Lighting Applications Electrical | Lighting Diffusers | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792;ISO 1183 |
||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 7.0 g/10min | ASTM D1238 | ||
Molding Shrinkage, Flow(3.2 mm) | 0.60 - 0.80 % | Internal Method | ||
Water Absorption, Saturation(23 °C) | 0.35 % | ISO 62 | ||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.15 % | ISO 62 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | ||
5 mm/min | 2300 MPa 2230 MPa |
ASTM D638 ISO 527-2/1 |
Tensile Strength, Yield | ||
50 mm/min;Type I | 62.0 MPa 62.0 MPa |
ASTM D638 ISO 527-2/50 |
Tensile Strength, Break | ||
50 mm/min;Type I | 65.0 MPa 58.0 MPa |
ASTM D638 ISO 527-2/50 |
Tensile Elongation, Yield | ||
50 mm/min;Type I | 6.0 % 6.0 % |
ASTM D638 ISO 527-2/50 |
Tensile Elongation, Break | ||
50 mm/min;Type I | 80 % 77 % |
ASTM D638 ISO 527-2/50 |
Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min |
2160 MPa 2250 MPa |
ASTM D790 ISO 178 |
Flexural Stress, at Break(13 mm/min) | 95.0 MPa | ISO 178 |
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 95.0 MPa | ASTM D790 |
Notched Izod Impact 23 °C 23 °C;80*10*3 mm |
450 J/m 65 kJ/m² |
ASTM D256 ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 70.0 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 1.8 MPa;3.2 mm 80*10*4 mm;1.8 MPa;4 mm;64 mm;Span |
125 °C 125 °C |
ASTM D648 ISO 75-2/Af |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 141 °C | ASTM D1525 |
Ball Pressure Test(123 - 127 °C) | Pass | IEC 60695-10-2 |
CLTE, Flow(-40 - 40 °C) | 6.8E-5 cm/cm/°C | ASTM E831 |
CLTE, Transverse(-40 - 40 °C) | 6.7E-5 cm/cm/°C | ASTM E831 |
Flame Rating(1.5 mm) | V-0 | UL 94 |
Glow Wire Flammability Index(1 mm) | 960 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 1 mm 1.5 mm |
850 °C 850 °C |
IEC 60695-2-13 |
Electrical | Nominal Value | Test Method |
Comparative Tracking Index, CTI | PLC 3 | UL 746 |
High Amp Arc Ignition, HAI, Surface | PLC 1 | UL 746 |
Hot-wire Ignition, HWI | PLC 3 | UL 746 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Rear Temperature<Injection> | 260 - 280 °C | |
Middle Temperature<injection> | 270 - 290 °C | |
Front Temperature<Injection> | 280 - 310 °C | |
Nozzle Temperature<Injection> | 270 - 290 °C | |
Processing Temp, Melt<Injection> | 280 - 310 °C | |
Mold Temperature<Injection> | 80 - 110 °C |